V content reduced dual two-phase Ni3Al-Ni3V intermetallic alloys

被引：8
作者：
Hashimoto, Takahiro [1 ]
Moronaga, Takuya [2 ]
Kaneno, Yasuyuki [1 ]
Takasugi, Takayuki [1 ]
机构：
[1] Osaka Prefecture Univ, Grad Sch Engn, Dept Mat Sci, Naka Ku, Sakai, Osaka 5998531, Japan
[2] Kobelco Res Inst Inc, Kobe, Hyogo 6510073, Japan
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2014年 / 596卷
关键词：
Multiphase intermetallics; Microstructure; Ni3V; Ni3Al; Alloy design; Phase stability; PACKED NI3X X; PHASE RELATION; MECHANICAL-PROPERTIES; MICROSTRUCTURAL EVOLUTION; AL; PROPERTY; TI; HARDNESS;
D O I：
10.1016/j.msea.2013.12.045
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The objective of this study is to reduce V content of Ni-base dual two-phase intermetallic alloy, with keeping the dual two-phase microstructure and also without sacrificing their mechanical and chemical properties. The dual two-phase microstructure was maintained when Cr and Nb instead of V were added to the alloy and their valence electron concentration (e/a) ranges from 8.59 to 8.43. Consequently, the contents of V in the dual two-phase intermetallic alloy were reduced by 8 at%, 8 at%, and 3 at% by Cr substitutions for V-site, both of Ni- and V-sites, and Ni-site, respectively. The density of the modified alloys slightly increased from that of the base alloy. Hardness was higher in the modified alloys than in the base alloy. The flow strength of the modified alloys is much improved from that of the base alloy in a wide range of temperatures. Also, oxidation resistance of the modified alloys was superior to those of the base alloy. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码：207 / 215
页数：9
相关论文
共 23 条
[11]   Phase relation and microstructure in multi-phase intermetallic alloys based on Ni3Al-Ni3Ti-Ni3V pseudo-ternary alloy system [J].
Nunomura, Y ;
Kaneno, Y ;
Tsuda, H ;
Takasugi, T .
INTERMETALLICS, 2004, 12 (04) :389-399
[12]   Microstructure, mechanical property and chemical property in Ni3Al-Ni3Ti-Ni3Nb-based multi-intermetallic alloys [J].
Ohira, K ;
Kaneno, Y ;
Takasugi, T .
JOURNAL OF MATERIALS SCIENCE, 2004, 39 (07) :2295-2301
[13]   The Corrosion Behavior of Ni3Al/Ni3V Two-Phase Intermetallic Compounds in Various Acidic Solutions [J].
Priyotomo, Gadang ;
Momono, Hideyuki ;
Wagle, Sanat ;
Okitsu, Kenji ;
Iwase, Akihiro ;
Kaneno, Yasuyuki ;
Nishimura, Rokuro ;
Takasugi, Takayuki .
INTERNATIONAL JOURNAL OF CORROSION, 2012, 2012
[14]   Microstructural evolution of dual multi-phase intermetallic alloys composed of geometrically close packed Ni3X (X: Al and V) type structures [J].
Shibuya, S. ;
Kaneno, Y. ;
Tsuda, H. ;
Takasugi, T. .
INTERMETALLICS, 2007, 15 (03) :338-348
[15]   Mechanical properties of dual multi-phase single-crystal intermetallic alloy composed of geometrically close packed Ni3X (X: Al and V) type structures [J].
Shibuya, S. ;
Kaneno, Y. ;
Yoshida, M. ;
Shishido, T. ;
Takasugi, T. .
INTERMETALLICS, 2007, 15 (02) :119-127
[16]   Dual multi-phase intermetallic alloys composed of geometrically close packed Ni3X (X: Al, Ti and V) type structures -: II.: Mechanical properties [J].
Shibuya, S ;
Kaneno, Y ;
Yoshida, M ;
Takasugi, T .
ACTA MATERIALIA, 2006, 54 (03) :861-870
[17]  
SINHA AK, 1972, PROG MATER SCI, V15, P79
[18]   Microstructure and mechanical property in dual two-phase intermetallic alloys composed of geometrically close-packed Ni3X (X: Al and V) containing Nb [J].
Soga, W. ;
Kaneno, Y. ;
Yoshida, M. ;
Takasugi, T. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 473 (1-2) :180-188
[19]   Phase relation and microstructure in multi-phase intermetallic alloys based on Ni3Al-Ni3Nb-Ni3V pseudo-ternary alloy system [J].
Soga, W ;
Kaneno, Y ;
Takasugi, T .
INTERMETALLICS, 2006, 14 (02) :170-179
[20]   Alloying behavior of Ni3M-type GCP compounds [J].
Sugimura, H. ;
Kaneno, Y. ;
Takasugi, T. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 496 (1-2) :116-121
123