Fatigue and Damage in Structural Materials Studied by X-Ray Tomography

被引：136

作者：

Withers, Philip J. ^{[1
]}

Preuss, Michael ^{[1
]}

机构：

[1] Univ Manchester, Sch Mat, Manchester M13 9PL, Lancs, England

来源：

ANNUAL REVIEW OF MATERIALS RESEARCH, VOL 42 | 2012年 / 42卷

基金：

英国工程与自然科学研究理事会;

关键词：

X-ray computed tomography (CT); fatigue crack; damage accumulation; stress corrosion cracking (SCC); RESOLUTION COMPUTED-TOMOGRAPHY; STRESS-CORROSION CRACKS; IN-SITU; SYNCHROTRON-RADIATION; CREEP CAVITATION; GRAIN-BOUNDARIES; INTERNAL DAMAGE; MICROTOMOGRAPHY; FRACTURE; CLOSURE;

D O I：

10.1146/annurev-matsci-070511-155111

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This paper reviews progress using X-ray computed tomography to study damage accumulation. Since its introduction, X-ray microtomography has been used to diagnose the presence of damage. In this review, a wide range of damage-accumulation mechanisms are covered including cavitation, fracture, microcracking, fatigue cracking, and stress corrosion cracking. In this regard, the advantages of attenuation and phase contrast imaging are discussed. This review includes both measurements of damage accumulation, taken postmortem, and the incremental monitoring of damage-accumulation processes during life (sometimes termed four-dimensional tomography). In addition to the qualitative diagnostic studies, the quantitative analysis of tomography images to extract key failure parameters is examined.

引用

页码：81 / 103

页数：23

共 50 条

[41] Neural network segmentation methods for fatigue crack images obtained with X-ray tomography [J].

Xiao, Ce ;

Buffiere, Jean-Yves .

ENGINEERING FRACTURE MECHANICS, 2021, 252

[42] Fast X-ray micro-tomography for low-Z materials [J].

Xu, L. ;

Chen, R. ;

Du, G. ;

Xie, H. ;

Xiao, T. .

JOURNAL OF INSTRUMENTATION, 2015, 10

[43] Hygrothermal progressive damage in open-hole compression of composite laminates with aligned carbon nanotube interlaminar reinforcement studied by X-ray micro-computed tomography [J].

Kopp, Reed ;

Ni, Xinchen ;

Nordin, Pontus ;

Hallander, Per ;

Selegard, Linnea ;

Wardle, Brian L. .

COMPOSITES PART B-ENGINEERING, 2024, 278

[44] X-ray microtome by fluorescence tomography [J].

Simionovici, A ;

Chukalina, M ;

Günzler, F ;

Schroer, C ;

Snigirev, A ;

Snigireva, I ;

Tümmler, J ;

Weitkamp, T .

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION A-ACCELERATORS SPECTROMETERS DETECTORS AND ASSOCIATED EQUIPMENT, 2001, 467 :889-892

[45] Revelation of microcracks as tooth structural element by X-ray tomography and machine learning [J].

Dumbryte, Irma ;

Narbutis, Donatas ;

Vailionis, Arturas ;

Juodkazis, Saulius ;

Malinauskas, Mangirdas .

SCIENTIFIC REPORTS, 2022, 12 (01)

[46] Microstructure of out-of-pile annealed neutron irradiated beryllium studied by X-ray tomography [J].

Vladimirov, P. ;

Ferrero, C. ;

Chakin, V. ;

Kurinskiy, P. ;

Moeslang, A. ;

Pieritz, R. ;

Weitkamp, T. ;

Brun, E. .

ACTA MATERIALIA, 2015, 88 :293-301

[47] Investigation of ductile damage in dual phase steel during tensile deformation by in situ X-ray computed tomography [J].

Chen, Jiadong ;

Magdysyuk, Oxana, V ;

Li, Xiao ;

Withers, Philip J. ;

Yan, Kun .

ENGINEERING FRACTURE MECHANICS, 2023, 293

[48] CHALLENGES ASSOCIATED WITH THE QUANTITATIVE ANALYSIS OF DUCTILE DAMAGE USING X-RAY COMPUTED TOMOGRAPHY [J].

Cooper, Adam J. ;

Burnett, Timothy L. ;

Tuck, Olivia C. G. ;

Sherry, Andrew H. .

PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, 2018, VOL 6B, 2019,

[49] Quantifying damage in polycrystalline ice via X-Ray computed micro-tomography [J].

Hammonds, Kevin ;

Baker, Ian .

ACTA MATERIALIA, 2017, 127 :463-470

[50] X-Ray Phase-Contrast Tomography of Renal Ischemia-Reperfusion Damage [J].

Velroyen, Astrid ;

Bech, Martin ;

Zanette, Irene ;

Schwarz, Jolanda ;

Rack, Alexander ;

Tympner, Christiane ;

Herrler, Tanja ;

Staab-Weijnitz, Claudia ;

Braunagel, Margarita ;

Reiser, Maximilian ;

Bamberg, Fabian ;

Pfeiffer, Franz ;

Notohamiprodjo, Mike .

PLOS ONE, 2014, 9 (10)

← 1 2 3 4 5 →