Friction and wear processes modification of ion implanted steel

被引：0

作者：

Kamienska-Krzowska, B ^{[1
]}

Tarkowski, P ^{[1
]}

机构：

[1] Tech Univ Lublin, Mech Fac, PL-20618 Lublin, Poland

来源：

NUKLEONIKA | 1999年 / 44卷 / 02期

关键词：

D O I：

暂无

中图分类号：

O61 [无机化学];

学科分类号：

070301 ; 081704 ;

摘要：

Comparative studies of implanted and non-implanted specimens are carried out as model experiments at the test stand according to different testing methods. Tested specimens were produced of 15 HGM steel and were implanted with a nitrogen dose of 2X10(17) ions/cm(2) with 120 keV. The results of the study indicate that nitrogen ion implantation of the 15 HGM steel improves the friction coefficient and wear intensity.