Influence of high current pulsed electron beam treatment on the tribological properties of Al-Si-Pb alloy

被引：15

作者：

An, J ^{[1
]}

Shen, XX ^{[1
]}

Lu, Y ^{[1
]}

Liu, YB ^{[1
]}

Li, RG ^{[1
]}

Chen, CM ^{[1
]}

Zhang, MJ ^{[1
]}

机构：

[1] Jilin Univ, Key Lab Automobile Mat, Minist Educ, Dept Mat Sci & Engn, Changchun 130025, Peoples R China

来源：

SURFACE & COATINGS TECHNOLOGY | 2006年 / 200卷 / 18-19期

基金：

中国国家自然科学基金;

关键词：

pulsed electron beam; coefficient of friction; wear rate; film of lubricant;

D O I：

10.1016/j.surfcoat.2005.07.106

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The tribological properties of Al-Si-Pb alloys irradiated by high current electron beam (HCPEB) were investigated under dry sliding conditions using a pin-on-disc type wear testing machine. The HCPEB parameters used to treat the samples are: electron energy: 21-25 keV; energy density: 1.5-2.5 J/cm(2); pulse duration: 1.5 mu s; number of pulses: 15. The results show that the microstructure and mechanical properties can be greatly improved. These factors contribute to great increase in wear resistance of HCPEB irradiated Al-Si-Pb alloys at 2.0 J/cm(2) and 2.5 J/cm(2). Optical observation and X-ray photoelectron spectroscopy (XPS) analysis reveal that the low wear rate and lowest level in coefficient of friction at high load levels for Al-Si-Pb alloys HCPEB irradiated with more than 1.5 J/cm(2) are due to a film of lubricant covering almost the entire worn surface. This film is a mixture of different constituents containing Al, Fe, Si, O and Ph, in which Ph exists in the form of Pb4SiO6. With the applied load increased, the dominant wear modes exhibit successively the oxidative wear, film spalling, and adhesive wear. (c) 2005 Elsevier B.V. All rights reserved.

引用

页码：5590 / 5597