Processing and compressive creep of cast replicated IN792 Ni-base superalloy foams

被引：13
|
作者：
DeFouw, John D. [1 ]
Dunand, David C. [1 ]
机构：
[1] Northwestern Univ, Dept Mat Sci & Engn, Evanston, IL 60208 USA
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2012年 / 558卷
关键词：
Mechanical characterization; Cellular materials; Nickel based superalloys; Casting; MECHANICAL-PROPERTIES; MICROSTRUCTURE; DEFORMATION;
D O I：
10.1016/j.msea.2012.07.099
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Nickel-base superalloy foams were created by a casting replication technique where a lightly sintered preform of SrF2 was pressure infiltrated with molten IN792; after solidification of the composite, the salt phase was dissolved with HCl to create 65% open porosity. Room temperature yield strength and stiffness of the IN792 foam compared well with existing models. Monolithic and foam samples were tested under creep conditions at 750 and 850 degrees C at stresses ranging from 5 to 40 MPa for the foams and from 150 to 650 MPa for the monolithic alloy. Both exhibited power-law creep behavior at high stresses and a transition to viscous flow at lower stresses, which was modeled using equations for dislocation and diffusional creep. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码：129 / 133
页数：5
相关论文
共 50 条
  • [31] Microstructure evolution and mechanical properties of a new cast Ni-base superalloy with various Ti contents
    Ou, Meiqiong
    Ma, Yingche
    Ge, Hualong
    Xing, Weiwei
    Zhou, Yangtao
    Zheng, Shijian
    Liu, Kui
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 735 : 193 - 201
  • [32] Creep behavior and deformation mechanisms of a novel directionally solidified Ni-base superalloy at 900 °C
    Zhang, P.
    Li, J.
    Gong, X. F.
    Yuan, Y.
    Gu, Y. F.
    Wang, J. C.
    Yan, J. B.
    Yin, H. F.
    MATERIALS CHARACTERIZATION, 2019, 148 : 201 - 207
  • [33] Investigation of Solidification and Segregation Characteristics of Cast Ni-Base Superalloy K417G
    Gong, Li
    Chen, Bo
    Du, Zhanhui
    Zhang, Mengshu
    Liu, Ruichang
    Liu, Kui
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (03) : 541 - 550
  • [34] Long-term thermal exposure responses of the microstructure and properties of a cast Ni-base superalloy
    Qin, X. Z.
    Guo, J. T.
    Yuan, C.
    Hou, J. S.
    Zhou, L. Z.
    Ye, H. Q.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 543 : 121 - 128
  • [35] Influence of thermal exposure on microstructural stability and tensile properties of a new Ni-base superalloy
    Liu, Hao
    Zhao, Xinbao
    Yuan, Yong
    Dang, Yingying
    Li, Weiqi
    Xu, Jiachen
    Cheng, Yuan
    Yue, Quanzhao
    Gu, Yuefeng
    Zhang, Ze
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 21 : 4462 - 4472
  • [36] The effect of stress, temperature and loading direction on the creep behaviour of Ni-base single crystal superalloy miniature tensile specimens
    Wollgramm, P.
    Buerger, D.
    Parsa, A. B.
    Neuking, K.
    Eggeler, G.
    MATERIALS AT HIGH TEMPERATURES, 2016, 33 (4-5) : 346 - 360
  • [37] Effect of Ti and Ta on hot cracking susceptibility of directionally solidified Ni-based superalloy IN792
    Zhang, J
    SCRIPTA MATERIALIA, 2003, 48 (06) : 677 - 681
  • [38] Tensile deformation behavior of a new Ni-base superalloy at room temperature
    Zhang, P.
    Yuan, Y.
    Li, B.
    Guo, S. W.
    Yang, G. X.
    Song, X. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 655 : 152 - 159
  • [39] High temperature strength and failure of the Ni-base superalloy PM 3030
    Nganbe, Michel
    Heilmaier, Martin
    INTERNATIONAL JOURNAL OF PLASTICITY, 2009, 25 (05) : 822 - 837
  • [40] Intergranular crack tip oxidation in a Ni-base superalloy
    Viskari, L.
    Hornqvist, M.
    Moore, K. L.
    Cao, Y.
    Stiller, K.
    ACTA MATERIALIA, 2013, 61 (10) : 3630 - 3639
12345