The effect of vacuum heat treatment on the oxidation behavior of APS thermal barrier coating

被引：2

作者：

Chen, Y. J. ^{[1
,3
]}

Liu, S. Q. ^{[2
]}

Lin, X. P. ^{[2
]}

Wang, Z. P. ^{[1
]}

Wang, L. J. ^{[3
]}

机构：

[1] Civil Aviat Univ China, Tianjin, Peoples R China

[2] Hebei Univ Technol, Tianjin, Peoples R China

[3] Tianjin Univ, Tianjin, Peoples R China

来源：

ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷

基金：

中国国家自然科学基金;

关键词：

Vacuum heat treatment; TBC; oxidation; thermally grown oxide; APS; PREOXIDATION; SYSTEMS;

D O I：

10.4028/www.scientific.net/AMR.239-242.3127

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Thermal barrier coating (TBC), which consisted of a NiCoCrAlY bond coat (BC) and a ZrO2-8 wt.%Y2O3 topcoat (TC), was fabricated on the nickel-base superalloy by air plasma spray (APS). The BC and TBC was treated by vacuum heat treatment (VHT). The oxidation of coating with and without VHT has been performed at 1050 degrees C. Oxidation behavior of coatings and thermally grown oxide(TGO) scale were studied by SEM with EDS. As shown in the results, after treating by VHT, a continuous Al2O3 layer formed more rapidly on the VHT coating than that formed on the APS coating, which can act as a diffusion barrier to suppress the formation of other detrimental oxides. The pre-oxidation treatments reduced the growth rate and extend the steady-state growth stage. The TOO in VHT TBC was still a single layer Al2O3 oxide after 120h. However, after same oxidation time, the TGO in APS TBC produced a dual-layer oxide consisting of an inner Al2O3 layer and outer spinet layer. Therefore the VHT improves the oxidation resistance of APS coating.

引用

页码：3127 / +

页数：2

共 11 条

[1] Pre-oxidation and TGO growth behaviour of an air-plasma-sprayed thermal barrier coating
Chen, W. R.
Wu, X.
Marple, B. R.
Lima, R. S.
Patnaik, P. C.
[J]. SURFACE & COATINGS TECHNOLOGY, 2008, 202 (16) : 3787 - 3796
[2] Oxide and TBC spallation in β-NiAl coated systems under mechanical loading
Harvey, M.
Courcier, C.
Maurel, V.
Remy, L.
[J]. SURFACE & COATINGS TECHNOLOGY, 2008, 203 (5-7) : 432 - 436
[3] Simulation of stresses and delamination in a plasma-sprayed thermal barrier system upon thermal cycling
He, MY
Hutchinson, JW
Evans, AG
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 345 (1-2): : 172 - 178
[4] FAILURE MECHANISMS OF THERMAL BARRIER COATINGS EXPOSED TO ELEVATED-TEMPERATURES
MILLER, RA
LOWELL, CE
[J]. THIN SOLID FILMS, 1982, 95 (03) : 265 - 273
[5] Effects of bond-coat preoxidation and surface finish on isothermal and cyclic oxidation, high temperature corrosion and thermal shock resistance of TBC systems
Monceau, D
Crabos, F
Malié, A
Pieraggi, B
[J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 : 607 - 614
[6] The Effect of Heat Treatment on the Oxidation Behavior of HVOF and VPS CoNiCrAlY Coatings
Saeidi, S.
Voisey, K. T.
McCartney, D. G.
[J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2009, 18 (02) : 209 - 216
[7] Failure modes in plasma-sprayed thermal barrier coatings
Schlichting, KW
Padture, NP
Jordan, EH
Gell, M
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 342 (1-2): : 120 - 130
[8] Failure analysis of high-temperature oxidation for plasma sprayed thermal barrier coating systems with different coating characteristics
Takahashi, S
Yoshiba, M
Harada, Y
[J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 6, PRT 1 AND 2, PROCEEDINGS, 2004, 461-464 : 367 - 374
[9] SOME LIMITING FACTORS IN USE OF ALLOYS AT HIGH TEMPERATURES
WALLWORK, GR
HED, AZ
[J]. OXIDATION OF METALS, 1971, 3 (02): : 171 - &
[10] The behavior of MCrAlY coatings on Ni3Al-base superalloy
Wang, B
Gong, J
Sun, C
Huang, RF
Wen, LS
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 357 (1-2): : 39 - 44

← 1 2 →