Synthesis of porous platinum nanoparticles

被引：224

作者：

Teng, XW ^{[1
]}

Liang, XY ^{[1
]}

Maksimuk, S ^{[1
]}

Yang, H ^{[1
]}

机构：

[1] Univ Rochester, Dept Chem Engn, Rochester, NY 14627 USA

来源：

SMALL | 2006年 / 2卷 / 02期

关键词：

methanol oxidation; nanostructures; platinum; porous materials; self-assembly;

D O I：

10.1002/smll.200500244

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

The synthesis of nearly monodisperse porous Pt nanoparticles through a self-organization process, was illustrated. The synthesis was conducted in diphenyl ether (DPE) using platinum acetylacetone as the precursor and 1, 2-hexadocanediol (HDD) as the reducing agent. The electrochemical measurements were conducted at room temperature using a three-electrode cell on a CHI 760 dual-channel-electrochemical workstation. The results show that the shifts of the peak potentials were within 0.01 V with the increase in temperature.

引用

页码：249 / 253

页数：5

共 31 条

[1] Shape-controlled synthesis of colloidal platinum nanoparticles [J].

Ahmadi, TS ;

Wang, ZL ;

Green, TC ;

Henglein, A ;

ElSayed, MA .

SCIENCE, 1996, 272 (5270) :1924-1926

[2] ELECTROOXIDATION OF METHANOL ON PLATINUM BONDED TO THE SOLID POLYMER ELECTROLYTE, NAFION [J].

ARAMATA, A ;

KODERA, T ;

MASUDA, M .

JOURNAL OF APPLIED ELECTROCHEMISTRY, 1988, 18 (04) :577-582

[3] Mesoporous platinum films from lyotropic liquid crystalline phases [J].

Attard, GS ;

Bartlett, PN ;

Coleman, NRB ;

Elliott, JM ;

Owen, JR ;

Wang, JH .

SCIENCE, 1997, 278 (5339) :838-840

[4] Determination of nanocrystal sizes:: A comparison of TEM, SAXS, and XRD studies of highly monodisperse COPt3 particles [J].

Borchert, H ;

Shevehenko, EV ;

Robert, A ;

Mekis, I ;

Kornowski, A ;

Grübel, G ;

Weller, H .

LANGMUIR, 2005, 21 (05) :1931-1936

[5] ULTRAFINE AND SPECIFIC CATALYSTS AFFORDING EFFICIENT HYDROGEN EVOLUTION FROM WATER UNDER VISIBLE-LIGHT ILLUMINATION [J].

BRUGGER, PA ;

CUENDET, P ;

GRATZEL, M .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1981, 103 (11) :2923-2927

[6] Electrocatalytic activity of ordered intermetallic phases for fuel cell applications [J].

Casado-Rivera, E ;

Volpe, DJ ;

Alden, L ;

Lind, C ;

Downie, C ;

Vázquez-Alvarez, T ;

Angelo, ACD ;

DiSalvo, FJ ;

Abruña, HD .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2004, 126 (12) :4043-4049

[7]

Chen J., 2005, ANGEW CHEM, V117, P2645

[8] Polyol synthesis of platinum nanostructures: Control of morphology through the manipulation of reduction kinetics [J].

Chen, JY ;

Herricks, T ;

Xia, YN .

ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2005, 44 (17) :2589-2592

[9]

Cullity BD, 1978, ELEMENTS XRAY DIFFRA

[10]

Ficicioglu F, 1997, J ELECTROANAL CHEM, V430, P179

← 1 2 3 4 →