Synthesis of Wood Lignin-Urea-Formaldehyde Resin Adhesive

被引：12
|
作者：
Wang, Zhe [1 ]
Xue, Jingwen [1 ]
Qu, Jianbo
Liu, Wenxia [1 ]
机构：
[1] Shandong Polytech Univ, Minist Educ, Key Lab Paper Sci & Technol, Jinan 250353, Peoples R China
来源：
MATERIAL SCIENCES AND TECHNOLOGY, PTS 1 & 2 | 2012年 / 560-561卷
关键词：
lignin; urea-formaldehyde resin; binding strength; free formaldehyde;
D O I：
10.4028/www.scientific.net/AMR.560-561.242
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Lignin-urea-formaldehyde resin adhesive was synthesized with alkali lignin from gramineae waste pulping liquor. Alkali lignin was purified and hydroxymethylated with HCHO and then crosslinked with urea-formaldehyde resin, polyvinyl alcohol and melamine. Results showed that lignin content in purified alkali lignin was 86.91%, both binding strength and free HCHO content of urea-formaldehyde resin synthesized from hydroxymethylated lignin reached the optimum value. The proper lignin amount for preparing resin was 30%, and the binding strength at this condition was 4.56MPa, and free formaldehyde content was 0.049%.
引用
收藏
页码：242 / 246
页数：5
相关论文
共 50 条
  • [21] Urea-formaldehyde microspheres as a potential additive to wood adhesive
    Pinkl, Stefan
    van Herwijnen, Hendrikus W. G.
    Veigel, Stefan
    Gindl-Altmutter, Wolfgang
    Riegler, Martin
    JOURNAL OF WOOD SCIENCE, 2018, 64 (04) : 390 - 397
  • [22] Urea-formaldehyde microspheres as a potential additive to wood adhesive
    Stefan Pinkl
    Hendrikus W. G. van Herwijnen
    Stefan Veigel
    Wolfgang Gindl-Altmutter
    Martin Riegler
    Journal of Wood Science, 2018, 64 : 390 - 397
  • [23] Penetration of liquid urea-formaldehyde adhesive into beech wood
    Sernek, M
    Resnik, J
    Kamke, FA
    WOOD AND FIBER SCIENCE, 1999, 31 (01): : 41 - 48
  • [24] PRELIMINARY EXPERIMENTS WITH A MELAMINE-UREA-FORMALDEHYDE WOOD ADHESIVE
    KREIBICH, RE
    ADHESIVES AGE, 1976, 19 (10): : 27 - 29
  • [25] Characterization and phenolation of biorefinery technical lignins for lignin-phenol-formaldehyde resin adhesive synthesis
    Yang, Sheng
    Wen, Jia-Long
    Yuan, Tong-Qi
    Sun, Run-Cang
    RSC ADVANCES, 2014, 4 (101) : 57996 - 58004
  • [26] Utilization of carbon black from Mao bamboo as reinforcing agent for melamine urea formaldehyde resin wood adhesive
    Liu, Jinming
    Mo, Hailin
    Xie, Enjun
    Fang, Jianlin
    Hou, Zhibing
    Gan, Weixing
    Industrial Crops and Products, 2022, 187
  • [27] Utilization of carbon black from Mao bamboo as reinforcing agent for melamine urea formaldehyde resin wood adhesive
    Liu, Jinming
    Mo, Hailin
    Xie, Enjun
    Fang, Jianlin
    Hou, Zhibing
    Gan, Weixing
    INDUSTRIAL CROPS AND PRODUCTS, 2022, 187
  • [28] Progress in research on urea-formaldehyde resin of wood industry
    Institute of Chemical Industry of Forest Products, CAF, Key and Open Lab. on Forest Chemical Engineering, SFA, Nanjing 210042, China
    Linchan Huaxue Yu Gongye, 2006, 2 (122-126):
  • [29] Improving urea formaldehyde resin properties by glyoxalated soda bagasse lignin
    Younesi-Kordkheili, Hamed
    Kazemi-Najafi, Saeed
    Eshkiki, Rabi Behrooz
    Pizzi, Antonio
    EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS, 2015, 73 (01) : 77 - 85
  • [30] GLUCOSE, UREA, AND PHENOL-BASED ADHESIVE RESIN FOR WOOD
    CHRISTIANSEN, AW
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1987, 194 : 77 - CELL
12345