Innovative fabrication of porous titanium coating on titanium by cold spraying and vacuum sintering

被引：58

作者：

Sun, Jifeng ^{[1
]}

Han, Yong ^{[1
]}

Cui, Kai ^{[1
]}

机构：

[1] Xian Jiaotong Univ, State Key Lab Mech Behavior Mat, Xian 710049, Peoples R China

来源：

MATERIALS LETTERS | 2008年 / 62卷 / 21-22期

关键词：

porous titanium coating; cold spray; bond strength; structure; mechanical properties;

D O I：

10.1016/j.matlet.2008.04.011

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A porous titanium coating on titanium is fabricated by cold spraying "Mg+Ti" powders followed by vacuum sintering. The porous coating is interconnected, possesses the porosity of 48.6% with pore sizes in the range of 70-150 mu m, and firmly bonds to titanium substrate with a bond strength higher than 42 MPa. The bending Young's modulus and bending strength of the porous coating are 14.47 +/- 1.21 GPa and 106.93 +/- 10.79 MPa, respectively. The compressive Young's modulus and compressive yield strength of the porous coating are 3.99 +/- 0.12 GPa and 178.66 +/- 13.20 MPai, respectively. The porous titanium coating has sufficient strength and matched Young's modulus with nature natural bone for clinical use under load bearing conditions. (c) 2008 Elsevier B.V. All rights reserved.

引用

页码：3623 / 3625

页数：3

共 13 条

[1]

Gibson L.J., 1997, CELLULAR SOLIDS STRU, DOI DOI 10.1017/CBO9781139878326

[2] Pore diameter of more than 100 μm is not requisite for bone ingrowth in rabbits [J].

Itälä, AI ;

Ylänen, HO ;

Ekholm, C ;

Karlsson, KH ;

Aro, HT .

JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 2001, 58 (06) :679-683

[3]

Kim HM, 2000, J BIOMED MATER RES, V52, P553, DOI 10.1002/1097-4636(20001205)52:3<553::AID-JBM14>3.0.CO

[4]

2-X

[5] Low stiffness porous Ti structures for load-bearing implants [J].

Krishna, B. Vamsi ;

Bose, Susmita ;

Bandyopadhyay, Amit .

ACTA BIOMATERIALIA, 2007, 3 (06) :997-1006

[6] Titanium alloys in total joint replacement - a materials science perspective [J].

Long, M ;

Rack, HJ .

BIOMATERIALS, 1998, 19 (18) :1621-1639

[7] Mechanical properties of porous titanium compacts prepared by powder sintering [J].

Oh, IH ;

Nomura, N ;

Masahashi, N ;

Hanada, S .

SCRIPTA MATERIALIA, 2003, 49 (12) :1197-1202

[8] Pore throat size and connectivity determine bone and tissue ingrowth into porous implants: Three-dimensional micro-CT based structural analyses of porous bioactive titanium implants [J].

Otsuki, Bungo ;

Takemoto, Mitsuru ;

Fujibayashi, Shunsuke ;

Neo, Masashi ;

Kokubo, Tadashi ;

Nakamura, Takashi .

BIOMATERIALS, 2006, 27 (35) :5892-5900

[9]

PILLIAR RM, 1987, J BIOMED MATER RES-A, V21, P1

[10] Fabrication methods of porous metals for use in orthopaedic applications [J].

Ryan, G ;

Pandit, A ;

Apatsidis, DP .

BIOMATERIALS, 2006, 27 (13) :2651-2670

← 1 2 →