Microstructure and Cyclic Oxidation of Yttria-Stabilized Zirconia/Nanostructured ZrO2 9.5Y2O3 5.6Yb2O3 5.2Gd2O3 Thermal Barrier Coating at 1373 K

被引:13
作者
Bahamirian, M. [1 ]
Hadavi, S. M. M. [2 ]
Farvizi, M. [3 ]
Keyvani, A. [4 ]
Rahimipour, M. R. [3 ]
机构
[1] Yazd Univ, Dept Min & Met Engn, Yazd, Iran
[2] Univ Tarbiat Modares, Dept Mat Engn, Tehran, Iran
[3] Mat & Energy Res Ctr, Dept Ceram, Karaj, Iran
[4] Shahrekord Univ, Fac Technol & Engn, Dept Met & Mat Engn, Shahrekord, Iran
关键词
high-temperature oxidation; mechanical and thermomechanical properties; nanostructured ZrO2; 9.5Y(2)O(3) 5.6Yb(2)O(3)5.2Gd(2)O(3); TBCs; YSZ; THERMOMECHANICAL PROPERTIES; MECHANICAL-PROPERTIES; HOT CORROSION; ZIRCONIA COATINGS; ELASTIC-MODULUS; TBC COATINGS; BOND-COAT; BEHAVIOR; YSZ; POWDERS;
D O I
10.1007/s11665-020-05174-1
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This study is intended to improve the high-temperature oxidation of nano-ZGYbY: ZrO(2)9.5Y(2)O(3)5.6Yb(2)O(3)5.2Gd(2)O(3) in order to apply it in the new generation of defect cluster thermal barrier coatings (TBCs) through the employment of an intermediate conventional yttria-stabilized zirconia (micro-YSZ) layer between the bond coat (CoNiCrAlY) and top coat. The specimens were deposited with an atmospheric plasma spray (APS) process on IN738LC superalloy. The cyclic oxidation test was performed in air at 1373 K with 4 h in each cycle. The microstructure of the nano-ZGYbY was studied by field emission scanning electron microscopy, revealing the formation of a bimodal microstructure consisted of nanosized particles retained from the initial APS-processed nanopowder and columnar grains, whereas the microstructure of intermediate micro-YSZ layer consisted of columnar grain splats only. X-ray diffraction of TBCs confirmed the formation of non-transformable (t ') ZrO(2)phase (c/a root 2 < 1.01) as well as the stability of this phase after oxidation. Also, applying an intermediate conventional YSZ layer with a higher CTE and K-IC than that of nano-ZGYbY between the bond and top coats improved mechanical properties in new TBCs and it increased the oxidation life.
引用
收藏
页码:7080 / 7093
页数:14
相关论文
共 78 条
  • [11] Bahamirian M., 2013, IRAN J MATER SCI ENG, V10, P12
  • [12] Bahamirian SMMHM, 2020, J ASIAN CERAM SOC, V20, P30
  • [13] Damage mechanisms and lifetime behavior of plasma-sprayed thermal barrier coating systems for gas turbines - Part II: Modeling
    Beck, Tilmann
    Herzog, Roland
    Trunova, Olena
    Offermann, Marita
    Steinbrech, Rolf W.
    Singheiser, Lorenz
    [J]. SURFACE & COATINGS TECHNOLOGY, 2008, 202 (24) : 5901 - 5908
  • [14] Bose S., 2007, High Temperature Coatings, P155
  • [15] A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part I: Model formulation
    Busso, EP
    Lin, J
    Sakurai, S
    Nakayama, M
    [J]. ACTA MATERIALIA, 2001, 49 (09) : 1515 - 1528
  • [16] Ceramic materials for thermal barrier coatings
    Cao, XQ
    Vassen, R
    Stoever, D
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (01) : 1 - 10
  • [17] Carlsson K., 2007, STUDY FAILURE DEV TH
  • [18] Influence of feedstock and spraying parameters on the depositing efficiency and microhardness of plasma-sprayed zirconia coatings
    Chen, H
    Lee, SW
    Du, H
    Ding, CX
    Choi, CH
    [J]. MATERIALS LETTERS, 2004, 58 (7-8) : 1241 - 1245
  • [19] Investigation of the thermomechanical properties of a plasma-sprayed nanostructured zirconia coating
    Chen, H
    Zhou, XM
    Ding, CX
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2003, 23 (09) : 1449 - 1455
  • [20] Chicot D., 2010, Mechanical Properties of Ceramic by Indentation: Principle and Applications, Ceramic Materials