Microstructure and Tribocorrosion Behavior of Al2O3/Al Composite Coatings: Role of Al2O3Addition

Pure Al coating and Al(2)O(3)particles reinforced Al composite coatings were prepared by arc-spraying. The feedstocks were pure Al wires and Al-based cored wires containing 10, 20, 30 vol.% Al2O3, respectively. The evolutions of microstructure, porosity and microhardness of the coatings with different Al(2)O(3)contents were investigated. Microstructural analysis shows that the addition of Al(2)O(3)particles improves density and decreases the porosity of the coating. The average hardness of the composite coatings varies from 39 to 416.5 HV(0.1)as Al(2)O(3)content increases from 0 to 30 vol.%. However, the microhardness of the Al matrix in the coatings increases first and then decreases as a function of Al(2)O(3)contents. The tribocorrosion tests were performed under potentiodynamic polarization conditions in 3.5 wt.% NaCl solution. The cathodic shift of open circuit potential and the increase in current density are induced by sliding wear. Compared with pure Al coating, the Al(2)O(3)particles reinforced composite coatings display a lower wear rate and coefficient of friction. The Al-20 vol.%Al(2)O(3)composite coating shows superior resistance to tribocorrosion. The tribocorrosion mechanism of the composite coatings is delamination coupling of corrosion wear.