Densification and oxidation behavior of a novel TiB2-MoSi2-CrB2 composite

被引：35
作者：
Murthy, T. S. R. Ch. [1 ]
Sonber, J. K. [1 ]
Subramanian, C. [1 ]
Hubli, R. C. [1 ]
Krishnamurthy, N. [1 ]
Suri, A. K. [1 ]
机构：
[1] Bhabha Atom Res Ctr, Mat Grp, Bombay 400085, Maharashtra, India
来源：
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2013年 / 36卷
关键词：
TiB2; MoSi2; CrB2; Hot pressing; Microstructure; Oxidation; MECHANICAL-PROPERTIES; TITANIUM DIBORIDE; MONOLITHIC TIB2; MICROSTRUCTURE; RESISTANCE; AL2O3-TIB2; NITRIDE; CRB2;
D O I：
10.1016/j.ijrmhm.2012.09.006
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Titanium diboride (TiB2) composite with MoSi2 and CrB2 has been prepared and tested to possess excellent oxidation resistance. Dense composite pellets were fabricated by hot pressing of powder mixtures. Microstructural characterization was carried out by XRD and SEM. Hardness and fracture toughness values were measured. Extensive oxidation studies of the composites were also carried out. Density of >= 96% p(th) was obtained by hot pressing at 1800 degrees C under a pressure of 35 MPa for 1 h. Hardness and fracture toughness were in the range of 18-24 GPa and 35-4 MPa.m(1/2) respectively. Crack branching, deflection and bridging mechanisms were observed in the crack propagation paths. Isothermal and continuous oxidation studies of these composites up to 1000 degrees C showed improved oxidation resistance with the formation of protective glassy layer. TiO2, Cr2O3 and SiO2 phases were identified on the oxidized surface. Diffusion controlled mechanism of oxidation was observed in the composites. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：243 / 253
页数：11
相关论文
共 43 条
  • [1] ADAMSON AW, 1965, PHYS CHEM SURFACES, P565
  • [2] A CRITICAL-EVALUATION OF INDENTATION TECHNIQUES FOR MEASURING FRACTURE-TOUGHNESS .1. DIRECT CRACK MEASUREMENTS
    ANSTIS, GR
    CHANTIKUL, P
    LAWN, BR
    MARSHALL, DB
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (09) : 533 - 538
  • [3] Barin I., 1995, THERMOCHEMICAL DATA, VI
  • [4] Barin Ihsan., 1995, THERMOCHEMICAL DATA, V2
  • [5] Processing and properties of monolithic TiB2 based materials
    Basu, B.
    Raju, G. B.
    Suri, A. K.
    [J]. INTERNATIONAL MATERIALS REVIEWS, 2006, 51 (06) : 352 - 374
  • [6] Synthesis and sintering of TiB2 and TiB2-TiC composite under high pressure
    Bhaumik, SK
    Divakar, C
    Singh, AK
    Upadhyaya, GS
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 279 (1-2): : 275 - 281
  • [7] A TEM study on TiB2-20%MoSi2 composite:: Microstructure development and densification mechanism
    Biswas, K
    Basu, B
    Suri, AK
    Chattopadhyay, K
    [J]. SCRIPTA MATERIALIA, 2006, 54 (07) : 1363 - 1368
  • [8] CHARACTERIZATION AND OXIDATION RESISTANCE OF HOT-PRESSED CHROMIUM DIBORIDE
    EMILIANI, ML
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 172 (1-2): : 111 - 124
  • [9] Graziani T., 1994, Materials and Manufacturing Processes, V9, P767, DOI 10.1080/10426919408934945
  • [10] MICROWAVE SINTERING OF TITANIUM DIBORIDE
    HOLCOMBE, CE
    DYKES, NL
    [J]. JOURNAL OF MATERIALS SCIENCE, 1991, 26 (14) : 3730 - 3738
12345