Effect of Surface Roughness on Oxidation Resistance of Stainless Steel AISI 316Ti During Exposure at High Temperature

被引：17

作者：

Nowak, Wojciech J. ^{[1
]}

机构：

[1] Rzeszow Univ Technol, Fac Mech Engn & Aeronaut, Dept Mat Sci, Powstancow Warszawy 12, PL-35959 Rzeszow, Poland

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2020年 / 29卷 / 12期

关键词：

cyclic oxidation test; high temperature oxidation; lifetime; oxidation resistance; stainless steel; thermal shock test; BEHAVIOR; NI; ALLOYS; OXIDE; GROWTH;

D O I：

10.1007/s11665-020-05267-x

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In the present work, the influence of surface roughness on oxidation kinetics of AISI 316Ti stainless steel and its consequences in term of oxidation resistance were investigated. Namely, the effect of surface roughness on oxidation resistance was evaluated during different types of cyclic oxidation tests at 900 and 1000 degrees C. The obtained results revealed that alloy possessing higher surface roughness showed longer lifetime compared to that with lower surface roughness. It was also found that more severe cyclic conditions suppressed the positive effect of surface roughness on sample's lifetime. The better oxidation resistance of rougher alloy was correlated with suppressed formation of Fe-rich nodules on ground surfaces and explained by the combined effect of introduced defects in the near-surface region and possible increase in residual stresses caused by mechanical surface preparation.

引用

页码：8060 / 8069

页数：10

共 34 条

[1]

[Anonymous], 2012, DAT STAINL STEEL 1 4, P1

[2] Influence of Surface Mechanical Attrition Treatment on the oxidation behaviour of 316L stainless steel [J].

Benafia, S. ;

Retraint, D. ;

Brou, S. Yapi ;

Panicaud, B. ;

Poussard, J. L. Grosseau .

CORROSION SCIENCE, 2018, 136 :188-200

[3]

Bolelli G, 2020, WEAR, V15, P444

[4] Formation mechanism of multilayer aluminide coating on 316L stainless steel by low-temperature pack cementation [J].

Dong, Jian ;

Sun, Yanhui ;

He, Feiyu .

SURFACE & COATINGS TECHNOLOGY, 2019, 375 :833-838

[5]

Fajnor P., 2010, Mater. Eng, V17, P21

[6] OXIDATION OF NI-CR-AL ALLOYS BETWEEN 1000 DEGREES AND 1200 DEGREES C [J].

GIGGINS, CS ;

PETTIT, FS .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (11) :1782-&

[7] Competition between Kirkendall shift and backstress in interdiffusion revisited - simple analytic model [J].

Gusak, A. ;

Wierzba, B. ;

Danielewski, M. .

PHILOSOPHICAL MAGAZINE, 2014, 94 (10) :1153-1165

[8] Oxide growth and dissolution on 316L stainless steel during irradiation in high temperature water [J].

Hanbury, Rigel D. ;

Was, Gary S. .

CORROSION SCIENCE, 2019, 157 :305-311

[9] Isothermal and cyclic oxidation behavior of free standing MCrAlY coatings manufactured by high-velocity atmospheric plasma spraying [J].

Hejrani, E. ;

Sebold, D. ;

Nowak, W. J. ;

Mauer, G. ;

Naumenko, D. ;

Vassen, R. ;

Quadakkers, W. J. .

SURFACE & COATINGS TECHNOLOGY, 2017, 313 :191-201

[10] Spallation Behavior of Thermally Grown Nickel Oxide on Nickel [J].

Hou, P. Y. ;

Cannon, R. M. .

OXIDATION OF METALS, 2009, 71 (5-6) :237-256

← 1 2 3 4 →