A preliminary study on the effect of fine aggregate replacement with metakaolin on strength and abrasion resistance of concrete

The purpose of this experimental study is to conduct a feasibility of using metakaolin (MK) as fine aggregate replacement in concrete. Sand was partially replaced with MK at levels of 10%, 20%, 30%, 40% and 50%, by weight. A reference mixture was designed to have characteristic compressive strength of 30 MPa. Specimens were subjected to abrasion testing in accordance with Egyptian Standard specifications (ES: 269-2/2003). Tests on compressive strength, splitting tensile strength, unit weight density and abrasion were performed up to 500 days. The various decomposition phases formed were identified using X-ray diffraction (XRD). The morphology of the formed hydrates was studied using scanning electron microscopy (SEM). Test results indicated that compressive strength, splitting tensile strength and abrasion resistance of concrete mixtures increased with increasing content of fine aggregate replacement with MK up to 40% then decreased at 50% replacement level. Abrasion resistances of concrete improved by about 23.12%, 36.18% and 46.24% over reference mixture with 40% replacement level at ages of 28, 91 and 500 days, respectively. (C) 2013 Elsevier Ltd. All rights reserved.