High-cycle fatigue behavior of type 316L stainless steel

被引:45
作者
Huang, JY [1 ]
Yeh, JJ [1 ]
Jeng, SL [1 ]
Chen, CY [1 ]
Kuo, RC [1 ]
机构
[1] INER, Lungtan 325, Taiwan
关键词
high-cycle fatigue; stress ratio; subsize; constant life diagram; subgrain boundary;
D O I
10.2320/matertrans.47.409
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High-cycle fatigue tests were conducted to investigate the effects of temperature, stress ratio (R), specimen orientation, welding and specimen size on the fatigue behavior of type 316L stainless steel, The high-cycle fatigue test results indicated that the fatigue limits significantly decreased when the stress ratio (R) decreased. The corresponding fatigue limits were reduced to lower values when tests were conducted at 300 degrees C. compared to those obtained at room temperature. The fatigue behavior and fatigue limits of standard and subsize specimens were observed to be consistent at both room temperature and 300 degrees C. The constant life diagram was established from the S-N Curves acquired. The fatigue limit strongly depended on the materials strength, which was a function of specimen orientation. test temperature, and welding processes. The dimension of the fatigue damaged area on a fracture Surface increased as the stress ratio decreased. In the case of R = -1.0, the fatigue damaged region extended over the whole fracture surface. The subgrain boundaries after high-cycle fatigue tests were clearly demonstrated by their diffraction patterns, which were related to the dynamic recovery of multiple dislocations.
引用
收藏
页码:409 / 417
页数:9
相关论文
共 22 条
[1]  
ALLEN AJ, 1988, NP5590 EPRI, P1
[2]  
*ASTM E, 1997, 46696 ASTM E, P466
[3]   DISLOCATION-STRUCTURES AROUND PROPAGATING FATIGUE CRACKS IN IRON [J].
AWATANI, J ;
KATAGIRI, K ;
NAKAI, H .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (01) :111-116
[4]   THE ALPHA-FRINGE CONTRAST OF THIN TWINS IN RELATION TO THE ANOMALOUS WEAK-BEAM CONTRAST OF STACKING-FAULTS [J].
CHEN, CY ;
STOBBS, WM .
ULTRAMICROSCOPY, 1995, 58 (3-4) :289-305
[5]  
FORSYTH DR, 1997, AGING MANAGEMENT EVA, P30
[6]   MICROSTRUCTURAL EXAMINATION OF FATIGUE-CRACK TIP IN HIGH-STRENGTH STEEL [J].
FUKUOKA, C ;
YOSHIZAWA, H ;
NAKAGAWA, YG ;
LAPIDES, ME .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1993, 24 (10) :2209-2216
[7]   Microstructural evaluation of cumulative fatigue damage below the fatigue limit [J].
Fukuoka, C ;
Nakagawa, YG .
SCRIPTA MATERIALIA, 1996, 34 (09) :1497-1502
[8]   A REVIEW OF FATIGUE FAILURES IN LWR PLANTS IN JAPAN [J].
IIDA, K .
NUCLEAR ENGINEERING AND DESIGN, 1992, 138 (03) :297-312
[9]  
ITOW M, 1995, 7 INT S ENV DEGR MAT, P541
[10]  
JEELANI S, 1986, INT J FATIGUE, V3, P159