Compressive Behavior of Spark Plasma Sintered CNT Reinforced Al2124 and Al6061 Nanocomposites

被引：2
作者：
Saheb, Nouari [1 ]
机构：
[1] King Fahd Univ Petr & Minerals, Ctr Excellence Nanotechnol, Dept Mech Engn, Dhahran 31261, Saudi Arabia
来源：
ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3 | 2013年 / 652-654卷
关键词：
Spark plasma sintering; Aluminum Nanocomposites; Compressive strength; CARBON NANOTUBES; COMPOSITES;
D O I：
10.4028/www.scientific.net/AMR.652-654.33
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present study, compressive behavior of CNT reinforced Al2124 and Al6061 nanocomposites was investigated. The powders were sonicated for 30 minutes then ball milled at 200 rpm for 1 hour under argon environment. The ball milled slurry was dried and again was milled under same conditions for 15 min to disperse the agglomerated particles. The prepared powders were spark plasma sintered at 35 MPa and 450 degrees C. Sintered specimens with final dimensions of 6 mm diameter and 12 mm length were used as standard specimens for compression tests carried out at a compression rate of 0.5 mm/min. The effect of CNT addition on the compressive modulus, percentage compression, and compressive strength was investigated.
引用
收藏
页码：33 / +
页数：3
相关论文
共 50 条
  • [31] Spark-plasma-sintered BaTiO3/Al2O3 nanocomposites
    Zhan, GD
    Kuntz, J
    Wan, JL
    Garay, J
    Mukherjee, AK
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2): : 443 - 446
  • [32] Modeling Thermal Conductivity of Al-Ni, Al-Fe, and Al-Co Spark Plasma Sintered Alloys
    Bhagtani, P.
    Bichler, L.
    Bardelcik, A.
    Elsayed, A.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (15) : 6821 - 6832
  • [33] A Novel Investigation on Tensile Strength, Compressive Strength, Hardness and Corrosion Resistance of Al6061 Hybrid Composite Reinforced with 15% Weight Fraction of B4C+Fly Ash and Comparing the Outputs with As-Cast Al6061
    Vinoth, V.
    Bharathiraja, G.
    JOURNAL OF PHARMACEUTICAL NEGATIVE RESULTS, 2022, 13 : 769 - 778
  • [34] Spark plasma sintering of layered γ-Al2O3/graphene reinforced nanocomposites
    Shamshirgar, Ali Saffar
    Ivanov, Roman
    Hussainova, Irina
    PROCEEDINGS OF THE ESTONIAN ACADEMY OF SCIENCES, 2019, 68 (02) : 140 - 144
  • [35] Thermal Behavior of Spark Plasma Sintered Alumina-Based Nanocomposites
    Momohjimoh, I.
    Nouari, S.
    Hussein, M. A.
    Laoui, T.
    Al-Aqeeli, N.
    ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2019, 44 (06) : 6013 - 6028
  • [36] Investigations on the temperature-dependent tribological behaviour of spark plasma sintered CNT-304 SS self-lubricating nanocomposites
    Radhamani, A. V.
    Bhaumik, Shubrajit
    Lau, Hon Chung
    Kamaraj, M.
    Ramakrishna, S.
    TRIBOLOGY-MATERIALS SURFACES & INTERFACES, 2023, 17 (03) : 224 - 236
  • [37] Damage and wear resistance of Al2O3-CNT nanocomposites fabricated by spark plasma sintering
    Lee, Kee-Sung
    Jang, Byung-Koog
    Sakka, Yoshio
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2013, 121 (1418) : 867 - 872
  • [38] Indentation size effect and wear characteristics of spark plasma sintered, hard MWCNT/Al2O3 nanocomposites
    Sikder, P.
    Pramanick, A.
    Sarkar, S.
    Das, S.
    Dey, P. P.
    Das, P. K.
    ADVANCES IN APPLIED CERAMICS, 2015, 114 (08) : 448 - 455
  • [39] Microstructure, interfacial reaction behavior, and mechanical properties of Ti3AlC2 reinforced Al6061 composites
    Liu, Zhi-bin
    Bao, Jia-bao
    Hu, Wen-jie
    Yan, Hong
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2024, 34 (09) : 2756 - 2771
  • [40] Interfacial characteristics and fracture behavior of spark-plasma -sintered TiNi fiber-reinforced 2024Al matrix composites
    Dong, Peng
    Wang, Zhe
    Wang, Wenxian
    Chen, Shaoping
    Zhou, Jun
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 691 : 141 - 149
12345