Fabrication and properties of supersonic plasma sprayed Al2O3 coating on porous Si3N4 substrate

被引：26

作者：

Wang, Chao ^{[1
]}

Chen, Jiwei ^{[1
]}

Fan, Lei ^{[1
]}

Han, Zhihai ^{[1
]}

Wang, Hongjie ^{[1
]}

机构：

[1] Xi An Jiao Tong Univ, State Key Lab Mech Behav Mat, Xian 710049, Shannxi, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 559卷

基金：

中国国家自然科学基金;

关键词：

Porous Si3N4; Al2O3; coating; Supersonic plasma spraying; Porosity; Mechanical properties; MECHANICAL-PROPERTIES; MICROSTRUCTURE; POROSITY; HARDNESS; POWER;

D O I：

10.1016/j.msea.2012.09.015

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A dense Al2O3 coating was directly deposited on porous Si3N4 substrate by supersonic plasma spraying. The microstructure and interface bonding of supersonic plasma sprayed Al2O3 coating were investigated. The surface of coating displayed explicit splat morphologies with densely packed splats. The molten Al2O3 droplets infiltrated into the inner pores of porous Si3N4, and formed an intermediate layer with rod-like Si3N4 particles at the interface. As-received Al2O3 coating sealed the surface pores of porous Si3N4, and decreased the water absorption of porous Si3N4 obviously from 42.1% to 5.2%, but only with a slight decrease of the total porosity. The mechanical properties of porous Si3N4 were also improved due to Al2O3 coating. The flexural strength of porous Si3N4 increased slightly from 93.7 +/- 3.1 to 97.5 +/- 3.4 MPa, although it decreased obviously at the beginning of spraying due to mechanical erosion of Al2O3 droplets. The Vickers hardness of porous Si3N4 increased gradually from 465 +/- 20 to 1023 +/- 16 MPa with the deposition content of Al2O3 increasing. (C) 2012 Elsevier B.V. All rights reserved.

引用

页码：725 / 730

页数：6

共 22 条

[1]

Antsiferov V.N., 1989, REFRACT IND CERAM, V29, P410, DOI DOI 10.1007/BF01297628

[2] Structure-property differences between supersonic and conventional atmospheric plasma sprayed zirconia thermal barrier coatings [J].

Bai, Y. ;

Han, Z. H. ;

Li, H. Q. ;

Xu, C. ;

Xu, Y. L. ;

Ding, C. H. ;

Yang, J. F. .

SURFACE & COATINGS TECHNOLOGY, 2011, 205 (13-14) :3833-3839

[3]

Cordes SE.., 2012, TRIBOL IND, V34, P24

[4] High hardness alumina coatings prepared by low power plasma spraying [J].

Gao, Y ;

Xu, XL ;

Yan, ZJ ;

Xin, G .

SURFACE & COATINGS TECHNOLOGY, 2002, 154 (2-3) :189-193

[5] Development and implementation of plasma sprayed nanostructured ceramic coatings [J].

Gell, M ;

Jordan, EH ;

Sohn, YH ;

Goberman, D ;

Shaw, L ;

Xiao, TD .

SURFACE & COATINGS TECHNOLOGY, 2001, 146 :48-54

[6] Microstructure development of Al2O3-13wt.%TiO2 plasma sprayed coatings derived from nanocrystalline powders [J].

Goberman, D ;

Sohn, YH ;

Shaw, L ;

Jordan, E ;

Gell, M .

ACTA MATERIALIA, 2002, 50 (05) :1141-1152

[7]

Kawai C, 1997, J AM CERAM SOC, V80, P2705, DOI 10.1111/j.1151-2916.1997.tb03179.x

[8] Mechanical and dielectric properties of porous Si2N2O-Si3N4 in situ composites [J].

Li ShuQin ;

Pei YuChen ;

Yu ChangQing ;

Li JiaLu .

CERAMICS INTERNATIONAL, 2009, 35 (05) :1851-1854

[9] Comparison in microstructure and mechanical properties of porous Si3N4 ceramics with SiC and Si3N4 coatings [J].

Li, Xiangming ;

Yin, Xiaowei ;

Zhang, Litong ;

Pan, Tianhao .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 527 (1-2) :103-109

[10] Gas Pressure Sintering of Arbitrary Porous Silicon Nitride Ceramics with High Mechanical Strength [J].

Li, Yong ;

Chen, Fei ;

Li, Ling ;

Zhang, Weiru ;

Yu, Honglin ;

Shan, Yubo ;

Shen, Qiang ;

Jiang, Hongyi .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2010, 93 (06) :1565-1568

← 1 2 3 →