Microstructure characterization of in situ synthesized porous Si2N2O ceramics using spodumene additive

被引：18
|
作者：
Dong, Xue [1 ]
Liu, Jiachen [1 ]
Du, Haiyan [1 ]
Guo, Anran [1 ]
Liu, Mengxia [1 ]
机构：
[1] Tianjin Univ, Key Lab Adv Ceram & Machining Technol, Minist Educ, Sch Mat Sci & Engn, Tianjin 300072, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2013年 / 39卷 / 04期
基金：
中国国家自然科学基金;
关键词：
A; Sintering; Ceramics; Fibers; TBA-based gel-casting; RELATIVELY HIGH-STRENGTH; SILICA CERAMICS;
D O I：
10.1016/j.ceramint.2012.10.224
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Porous Si2N2O ceramics was synthesized by the tert-butyl alcohol-based gel-casting method at a relatively low temperature using Si3N4 and SiO2 powders as the starting materials and spodumene (LiAl(SiO3)(2)) as the sintering additive. Porous Si2N2O ceramics with relative high compressive strength (10.80 MPa) and high porosity (65.5%) were successfully fabricated. The microstructure of porous Si2N2O after sintering at different sintering regimes was studied. The fibers observed in the pores can increase the compressive strength and the specific surface area of the sample. (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：4657 / 4662
页数：6
相关论文
共 50 条
  • [21] Resistance of Si2N2O ceramics to oxidation and erosion of molten silica
    WANG Si qing(王思青) 1
    2. Biomaterials Engineering Center
    TransactionsofNonferrousMetalsSocietyofChina, 2000, (03) : 418 - 420
  • [22] Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres
    Zhang Xiaoyan
    Huo Wenlong
    Lan Tian
    Cui Jie
    Gan Ke
    Yan Shu
    Yang Jinlong
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 : 41 - 44
  • [23] Resistance of Si2N2O ceramics to oxidation and erosion of molten silica
    Wang, SQ
    Yan, YH
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2000, 10 (03) : 418 - 420
  • [24] Fabrication and properties of Si2N2O ceramics for microwave sintering furnace
    Fan, Bingbing
    Li, Wei
    Zhang, Fan
    Li, Hongxia
    Zhang, Rui
    Liu, Guoqi
    Qian, Fan
    Chen, Yongqiang
    PROCESSING AND APPLICATION OF CERAMICS, 2020, 14 (01) : 32 - 39
  • [25] PRESSURELESS-SINTERED CERAMICS BASED ON THE COMPOUND SI2N2O
    LEWIS, MH
    REED, CJ
    BUTLER, ND
    MATERIALS SCIENCE AND ENGINEERING, 1985, 71 (1-2): : 87 - 94
  • [26] Mechanical, dielectric properties and thermal shock resistance of porous Si2N2O/Si3N4 composite ceramics
    Wei Liting
    Yu Yinhu
    Jiao Jiao
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2018, 19 (02): : 126 - 129
  • [27] Microstructure and kinetics of formation of Si2N2O and Si3N4 into Si porous preforms by chemical vapor infiltration (CVI)
    de la Pena, J. L.
    Pech-Canul, M. I.
    CERAMICS INTERNATIONAL, 2007, 33 (07) : 1349 - 1356
  • [28] REFINEMENT OF THE STRUCTURE OF SI2N2O
    SJOBERG, J
    HELGESSON, G
    IDRESTEDT, I
    ACTA CRYSTALLOGRAPHICA SECTION C-CRYSTAL STRUCTURE COMMUNICATIONS, 1991, 47 : 2438 - 2441
  • [29] Effects of pore diameters on phase, oxidation resistance, and thermal shock resistance of the porous Si2N2O ceramics
    Lin, Shaojie
    Ye, Feng
    Ding, Junjie
    Yang, Chunping
    Ma, Jie
    Dong, Shangli
    Liu, Qiang
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2017, 100 (05) : 2190 - 2198
  • [30] Mechanical and Dielectric Properties of Si2N2O Ceramics Prepared by Pressureless Sintering
    Lin Xuping
    Ma Jingtao
    Tan Wei
    Zhang Baoqing
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 : 211 - 214
12345