Mechanical Properties of Phenol Formaldehyde Hybrid Composites Reinforced with Natural Cellulose Fibers

This paper reports on the preparation and mechanical properties of hybrid polymer composites involving areca fine fibers (AFFs), sisal fibers (SFs), and roselle fibers (RFs) as reinforcing agents in a phenol formaldehyde (PF) resin-based polymer matrix. For comparative study, an AFF/glass fiber-reinforced PF hybrid composite and AFF/PF composite were also prepared. Hybrid composites were fabricated using a hand lay-up technique, where the weight fraction of fibers was kept at 40 wt% at a ratio of 1: 1. Tensile and flexural properties of randomly oriented intimately mixed hybrid polymer composites were evaluated. The results revealed that the mechanical properties of the AFF/PF composite increased by a considerable amount when hybridized with the sisal fibers. Scanning electron microscopy (SEM) was used to analyze the fractured surface of the composite specimens after mechanical testing.