TENSILE TESTS OF ITER TF CONDUCTORS JACKET MATERIALS

被引:5
作者
Anashkin, O. P. [1 ]
Keilin, V. E. [1 ]
Krivykh, A. V. [1 ]
Diev, D. N. [1 ]
Dinisilov, A. S. [1 ]
Shcherbakov, V. I. [1 ]
Tronza, V. I. [2 ]
机构
[1] Kurchatov Inst, Russian Fed, Kurchatov Sq 1, Moscow 123182, Russia
[2] ITER Ctr Project Inst, Russian Fed, Moscow 123182, Russia
来源
ADVANCES IN CRYOGENIC ENGINEERING, VOL 58 | 2012年 / 1435卷
关键词
tensile tests; low temperature; stainless steel; serrated yielding; butt weld; LOW-TEMPERATURES;
D O I
10.1063/1.4712087
中图分类号
O59 [应用物理学];
学科分类号
摘要
The set of very tough requirements has been formulated for TF jacket materials with extremely high plasticity at liquid helium temperature. The stainless steel 316LN-IG is recommended to be used for TF jacket tubes. Samples of 316LN-IG tubes (whole tubes and sub-size samples) made of the material from the same electro slag remelt have been tested in different conditions -as received tubes and tubes after prescribed compaction, 2.5% deformation at room temperature and heat treatment at 650 degrees C, 200 hours. The tensile tests were carried out at room, liquid nitrogen and liquid helium temperatures down to 4.2 K, meeting corresponding ASME and ASTM requirements. The low temperature testing devices are described. The tests results for sub-size samples and whole tubes show that the latter tests are considerably more representative and important for butt weld qualification at LHe temperature. It was observed that the ferromagnetic properties of all samples and especially of butt welds increase with lowering the temperature and increasing the degree of deformation. At LHe temperature a non-uniform and highly localized serrated deformations were observed.
引用
收藏
页码:117 / 124
页数:8
相关论文
共 9 条
[1]  
Alekseev A., 2010, P INT SCI C DUR MAT, P1
[2]   OBSERVATION OF SERRATED DEFORMATION OF SUPERCONDUCTING MAGNETS WINDINGS [J].
ANASHKIN, OP ;
KEILIN, VE ;
KRIVIKH, AV .
CRYOGENICS, 1979, 19 (01) :31-32
[3]   Mechanical tests of ATLAS Barrel Toroid tie rods [J].
Anashkin, OP ;
Keilin, VE ;
Krivikh, AV ;
Lysenko, VV ;
Shcherbakov, VI ;
Dudarev, AV ;
ten Kate, HH ;
Mayri, C ;
Vedrine, P ;
Zaitsev, Y .
CRYOGENICS, 2005, 45 (07) :469-472
[4]  
DOLGIN AM, 1990, LOW TEMP PHYS, V16, P254
[5]  
Nikolaev V. I., 1997, SOLID STATE PHYS, V39, P647
[6]   EXPERIMENTAL-EVIDENCE ON THE DISLOCATION MECHANISM OF SERRATED YIELDING IN FCC METALS AND ALLOYS AT LOW-TEMPERATURES [J].
OBST, B ;
NYILAS, A .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 137 :141-150
[7]  
Obst B, 1998, ADV CRYOG ENG, V44, P331
[8]  
Pustovalov V. V., 2008, LOW TEMP PHYS, V34, P871
[9]  
Strizhalo V. A., 1993, PROBL PROCHN, P37