Looking over Liquid Silicone Rubbers: (1) Network Topology vs Chemical Formulations

被引:59
作者
Delebecq, Etienne [1 ]
Ganachaud, Francois [1 ,2 ,3 ]
机构
[1] Inst Charles Gerhardt, UMR 5076, F-34296 Montpellier, France
[2] Univ Lyon, F-69003 Lyon, France
[3] INSA Lyon, IMP, UMR5223, F-69621 Villeurbanne, France
关键词
liquid silicone rubber; platinum cured silicones; peroxide cured silicones; cross-linker structure; molar mass between cross-links; silicone hardness; MODEL POLY(DIMETHYLSILOXANE) NETWORKS; MECHANICAL-PROPERTIES; PENDANT CHAINS; CROSS-LINKER; HYDROSILYLATION; POLYDIMETHYLSILOXANE; ELASTOMERS; REINFORCEMENT; COPOLYMERS; SURFACE;
D O I
10.1021/am300502r
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
This study proposes a comprehensive study on liquid silicone rubber (LSR) formulations to unravel which components (among functional polydimethylsiloxane polymers and modified silica fillers) improve the mechanical properties of the final materials. In this first part, various industrial products have been deformulated using conventional chemical analyses. The silica content and their surface chemistry were assessed by TGA. Architecture and molar mass of polymers were deduced from Si-29 NMR and SEC in toluene, respectively. Relative concentrations of hydride and vinyl reactive groups and stoichiometric imbalance (r = n(SiH)/n(SiVi)) were quantified by proton NMR. Stoichiometric imbalance is slightly higher than 1.5 for cross linker with hydride functions well redistributed along the chain, whereas for some formulations, r's as high as 3.7 were implemented. These variations has. strong implications on the cross linking density of the final material, since the remaining hydride groups react together and decrease the molar mass between cross links From the comparison between formulations, it was shown that hardness adjustment is mainly performed by playing on two parameters: filler content and molar mass between cross linking points for hardness ranging from 20 to 30 Shore A. Above this limit, it is necessary to modify the silica surface with reactive groups, such as vinyl functions. Surprisingly, two formulations were shown to use a dual cross linking catalysis systems, peroxide and platinum, leading to efficient and full cure even at lower temperature (typically 140 degrees C). Network topologies were estimated from the predicted chemistry of the materials in a final discussion part.
引用
收藏
页码:3340 / 3352
页数:13
相关论文
共 63 条
[21]   Structure of hydrogen bonds and 1H NMR spectra of water at the interface of oxides [J].
Gun'ko, VM ;
Turov, VV .
LANGMUIR, 1999, 15 (19) :6405-6415
[22]  
HEDRICK JL, 1988, POLYM BULL, V19, P573
[23]  
Hurd D. T, 1954, Vinyl-Substitued Silica Aerogels, Patent No. [US2967168, 2967168]
[24]  
Jackson S., 2002, Method for preparing a silica suspension in a cross-linkable silicone rubber matrix, Patent No. [WO2002044259, 2002044259]
[25]  
Kammerer J., 1998, Liquid Compositions for Manufacture of Silicone Rubber Moldings with Improved Compression Set, Patent No. [US 5977249, 5977249]
[26]   Controlled destruction of residual crosslinker in a silicone elastomer for drug delivery [J].
Karlsson, A ;
Singh, SK ;
Albertsson, AC .
JOURNAL OF APPLIED POLYMER SCIENCE, 2002, 84 (12) :2254-2264
[27]  
Kim S.-H, 2007, Liquid Silicone Rubber Composition for Forming Breathable Coating Film on Textile and Process for Forming Breathable Coating Film on Textile, Patent No. [WO2007123379, 2007123379]
[28]  
Kim S.P., 2002, Method for Producing Release Film Using Silicone Aqueous Emulsion Release Liquid, Patent No. [US6737119, 6737119]
[29]  
Kim S.P., 2002, Method for Producing Release Film Using Silicone Aqueous Emulsion Release Liquid, Patent No. [10/320,715, 10320715]
[30]  
Kobayashi H., 1989, Method for Modifying the Surface of Finely Divided Silica, Patent No. [US4849022, 4849022]