Reaction mechanism between solid CaO and FeOx-CaO-SiO2-P2O5 slag at 1573 K

被引：96

作者：

Hamano, T ^{[1
]}

Fukagai, S ^{[1
]}

Tsukihashi, F ^{[1
]}

机构：

[1] Univ Tokyo, Grad Sch Frontier Sci, Dept Adv Mat Sci, Kashiwa, Chiba 2778561, Japan

来源：

ISIJ INTERNATIONAL | 2006年 / 46卷 / 04期

关键词：

CaO; dissolution; hot-metal; dephosphorization; FeOx-CaO-SiO2-P2O5; system; multi-phase flux;

D O I：

10.2355/isijinternational.46.490

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Solid CaO and FeOx-CaO-SiO2-P2O5 slag were reacted for 2 to 2 400 s at 1 573 K. The interface of CaO and slag were observed and analyzed by SEM/EDS. The CaO-FeO layer was formed beside solid CaO. The thickness of the CaO-FeO layer increased with time. Next to the CaO-FeO layer, 2CaO . SiO2 phase was formed in the melt and high content of FeO was included in the liquid. The activities of FeO and CaO for each phase were evaluated and reaction mechanism between solid CaO and FeOx-CaO-SiO2-P2O5 slag was discussed. The activity of FeO for 2CaO . SiO2 saturated melt is larger than that for the CaO-FeO layer, therefore, Fe2+ diffuses from slag phase to solid CaO. Then the CaO-FeO layer is formed beside solid CaO. The pass of the slag composition change accompanied by CaO dissolution are represented in the phase diagram for the FeOx-CaO-(SiO2 + P2O5) pseudo ternary system.

引用

页码：490 / 495

页数：6

共 17 条

[1]

[Anonymous], 1980, PHYS CHEM HIGH TEMPE

[2] MATHEMATICAL EXPRESSION OF SLAG METAL REACTIONS IN STEELMAKING PROCESS BY QUADRATIC FORMALISM BASED ON THE REGULAR SOLUTION MODEL [J].

BANYA, S .

ISIJ INTERNATIONAL, 1993, 33 (01) :2-11

[3]

CHIANG MH, 1988, AM CERAM SOC BULL, V67, P1222

[4] INVESTIGATIONS INTO DISSOLVING OF LIME SINGLE-CRYSTALS IN FEON-SIO2 HEATS [J].

HACHTEL, L ;

TROMEL, G ;

FIX, W .

ARCHIV FUR DAS EISENHUTTENWESEN, 1972, 43 (05) :361-&

[5]

Kimura H., 1974, J JPN I MET, V38, P226, DOI 10.2320/jinstmet1952.38.3_226

[6]

KOOPMANS P, 2000, P MOLT SLAGS FLUX SA

[7]

Matsushima M., 1976, TETSU TO HAGANE, V62, P182

[8]

NATALIE CA, 1979, IRONMAK STEELMAK, P101

[9] MECHANISM OF CAO DISSOLUTION INTO MELTS OF CAO-SIO2-FE2O3 AND CAO-SIO2-MGO SYSTEMS [J].

NOGUCHI, F ;

UEDA, Y ;

YANAGASE, T .

JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1977, 41 (09) :883-889

[10] STUDIES OF DISSOLUTION OF LIME CAO-FEO-SIO2-SLAGS [J].

OETERS, F ;

SCHEEL, R .

ARCHIV FUR DAS EISENHUTTENWESEN, 1974, 45 (09) :575-580

← 1 2 →