Microstructure and microtexture changes during solution nitriding to produce austenitic case on ferritic-austenitic duplex stainless steel

被引:17
作者
Padilha, AF [1 ]
Randle, V [1 ]
Machado, IF [1 ]
机构
[1] Univ Wales, Dept Mat Engn, Swansea, W Glam, Wales
关键词
D O I
10.1179/026708399101506869
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The present paper reports an investigation into the microstructural changes occurring in a ferritic-austenitic duplex stainless steel during solution nitriding. Both microstructure and microtexture modifications as a result of nitrogenation have been studied, in addition to the interaction between solution nitriding, grain growth, and texture. Three microstructural zones were identified. a duplex ferrite-austenite region overlayed by a transition zone overlayed again at the surface by an austenitic zone. The solution nitriding led to nitrogen enrichment at the specimen surface, which in turn enlarged the austenitic field in this region. The ferrite dissolution here triggered secondary recrystallisation, accompanied by a texture change. Hence, the texture of the austenite in this region was different from that in the duplex region. MST/4297.
引用
收藏
页码:1015 / 1018
页数:4
相关论文
共 22 条
[1]  
Berns H., 1994, HTM HAERTEREI TECHN, V49, P123, DOI [10.1515/htm-1994-490217, DOI 10.1515/HTM-1994-490217]
[2]  
CHAO H, 1967, T ASM, V10, P37
[3]  
CHIN GY, 1973, METALS HDB, V8, P229
[4]   FORMABILITY OF LOW-INTERSTITIAL 18 PCT CR-2 PCT MO FERRITIC STAINLESS-STEEL [J].
DAVISON, RM .
METALLURGICAL TRANSACTIONS, 1974, 5 (11) :2287-2294
[5]  
DELIMA NB, 1994, P INT C MET TECHN MA, V8, P405
[6]   COLD-ROLLING AND PRIMARY-RECRYSTALLISATION TEXTURES OF 18 PERCENT CHROMIUM STEELS CONTAINING 10 PERCENT, 12 PERCENT AND 14 PERCENT NICKEL [J].
DICKSON, MJ ;
GREEN, D .
MATERIALS SCIENCE AND ENGINEERING, 1969, 4 (05) :304-&
[7]   OVERVIEW .82. DEVELOPMENT OF TEXTURE AND MICROSTRUCTURE DURING COLD-ROLLING AND ANNEALING OF FCC ALLOYS - EXAMPLE OF AN AUSTENITIC STAINLESS-STEEL [J].
DONADILLE, C ;
VALLE, R ;
DERVIN, P ;
PENELLE, R .
ACTA METALLURGICA, 1989, 37 (06) :1547-1571
[8]  
GOODMAN SR, 1965, T METALL SOC AIME, V233, P103
[9]  
GOODMAN SR, 1964, T METALL SOC AIME, V230, P1413
[10]  
HUTCHINSON B, 1992, MATER SCI FORUM, V94, P385