A novel approach for strengthening Cu-Y2O3 composites by in situ reaction at liquidus temperature

被引:78
作者
Zhuo, Haiou [1 ]
Tang, Jiancheng [1 ]
Ye, Nan [1 ]
机构
[1] Nanchang Univ, Sch Mat Sci & Engn, Nanchang 330031, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 584卷
基金
中国国家自然科学基金;
关键词
Copper-based composite; In situ reaction; Microstructure; Strengthening mechanism; CU-CR; MECHANICAL-PROPERTIES; COPPER; MICROSTRUCTURE; REINFORCEMENT; ALLOYS;
D O I
10.1016/j.msea.2013.07.007
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Yttria (Y2O3) and most rare earth oxides are potentially attractive as dispersion for copper-based composites, owing to their thermodynamic stability. In this paper, Cu-0.9 vol% Y2O3 composites are prepared by in situ reaction at the liquidus temperature using Cu-0.4 wt% Y alloy. Transmission electron microscopy (TEM) observation indicates that Y2O3 nano-particles with a mean size of 5.0 nm and interspace of 20 nm are uniformly distributed in the copper m\atrix. Selected area diffraction (SAD) analysis shows there is a crystallographic orientation relationship of (422)(Y2O3)//((1) over bar1 (1) over bar)(Cu) and [01 (1) over bar](Y2O3)//[(1) over bar 12](Cu), indicating that the cubic Y2O3 phase is coherent with copper matrix. The ultimate tensile strength (UTS) of the prepared Cu-0.9Y(2)O(3) composites is 568 MPa, which are strengthened by grain-boundary strengthening, Orowan and shearing mechanism simultaneously. The analyses demonstrate that Orowan and shearing mechanism are the dominant strengthening mechanisms, and the calculated overall strength is in good agreement with the experimentally determined strength. (c) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码:1 / 6
页数:6
相关论文
共 32 条
[1]   Influence of heat treatment on tensile response of an oxide dispersion strengthened copper [J].
Al-Hajri, M ;
Melendez, A ;
Woods, R ;
Srivatsan, TS .
JOURNAL OF ALLOYS AND COMPOUNDS, 1999, 290 (1-2) :290-297
[2]  
[Anonymous], DISLOCATIONS SOLIDS
[3]  
[Anonymous], J PHASE EQUILIB
[4]   PRECIPITATION HARDENING [J].
ARDELL, AJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (12) :2131-2165
[5]  
Ashby M. F., 1969, PHYSICS STRENGTH PLA, P113
[6]   Creep deformation of dispersion-strengthened copper [J].
Broyles, SE ;
Anderson, KR ;
Groza, JR ;
Gibeling, JC .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (05) :1217-1227
[7]   Strengthening in rapidly solidified age hardened Cu-Cr and Cu-Cr-Zr alloys [J].
Correia, JB ;
Davies, HA ;
Sellars, CM .
ACTA MATERIALIA, 1997, 45 (01) :177-190
[8]   ELECTRICAL CONDUCTIVITY AND TENSILE STRENGTH OF DISPERSION-STRENGTHENED COPPER [J].
FUSCHILL.N ;
GIMPL, ML .
JOURNAL OF APPLIED PHYSICS, 1971, 42 (13) :5513-&
[9]   High temperature mechanical properties of Mg-Y2O3 composite:: Competition between texture and reinforcement contributions [J].
Garces, G. ;
Rodriguez, M. ;
Perez, P. ;
Adeva, P. .
COMPOSITES SCIENCE AND TECHNOLOGY, 2007, 67 (3-4) :632-637
[10]   ON CRITICAL RESOLVED SHEAR STRESS OF SOLID SOLUTIONS CONTAINING COHERENT PRECIPITATES [J].
GEROLD, V ;
HABERKORN, H .
PHYSICA STATUS SOLIDI, 1966, 16 (02) :675-&