Anodizing of pure magnesium in KOH-aluminate solutions under sparking

被引:163
|
作者
Khaselev, O [1 ]
Weiss, D
Yahalom, J
机构
[1] Technion Israel Inst Technol, Dept Mat Engn, IL-32000 Haifa, Israel
[2] Dead Sea Work Ltd, IL-84100 Beer Sheva, Israel
关键词
D O I
10.1149/1.1391838
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Anodizing of magnesium was studied in solutions containing 3 M KOH + 0.6 M KF + 0.21 M Na3PO4, with and without addition of 0.4 M and 1.1 M of aluminate. At constant applied current, the process occurs in two stages. First, the voltage rises linear ly until an initial breakdown occurs. A thin and compact oxide film is formed at this stage. In the second stage an intense continuous spark is maintained on the metal surface. A thick oxide film is formed at the site of sparking. The formation of the film is accompanied by voltage oscillation and gas evolution. The anodic films formed under continuous breakdown conditions are rough and porous and enriched in aluminum. Anodic films formed in a bath containing 1.1 M aluminate at 15 mA/cm(2) are composed of a single oxide phase MgAl2O4 spinel. (C) 1999 The Electrochemical Society. S0013-4651(98)09-036-3. All rights reserved.
引用
收藏
页码:1757 / 1761
页数:5
相关论文
共 50 条
  • [21] SINTERING CHARACTERISTICS OF MAGNESIUM ALUMINATE SPINEL PREPARED FROM PRECURSORY SOLUTIONS BY SPRAY DRYING AND CALCINING
    JONG, BW
    POWDER TECHNOLOGY, 1976, 15 (01) : 135 - 137
  • [22] Structural disordering in magnesium aluminate spinel compounds under ion-beam irradiation
    Matsumura, S
    Shimada, M
    Yasuda, K
    Kinoshita, C
    RADIATION EFFECTS AND ION-BEAM PROCESSING OF MATERIALS, 2004, 792 : 131 - 142
  • [23] Synthesis of Pure Magnesium Aluminate Spinel (MgAl2O4) from Waste Aluminum Dross
    Benkhelif, Ahmed
    Kolli, Mostafa
    WASTE AND BIOMASS VALORIZATION, 2022, 13 (05) : 2637 - 2649
  • [24] Synthesis of Pure Magnesium Aluminate Spinel (MgAl2O4) from Waste Aluminum Dross
    Ahmed Benkhelif
    Mostafa Kolli
    Waste and Biomass Valorization, 2022, 13 : 2637 - 2649
  • [25] Producing Pure Magnesium Through Silicothermic Under the Atmospheric Pressure
    Liu, Fei
    Yang, Bo
    Liu, Bo-Yu
    Li, Jiao
    Chang, Zhi-Min
    Shan, Zhi-Wei
    MAGNESIUM TECHNOLOGY 2020, 2020, : 309 - 312
  • [26] An impedance investigation of the mechanism of pure magnesium corrosion in sodium sulfate solutions
    Baril, Genevieve
    Galicia, Gonzalo
    Deslouis, Claude
    Pebere, Nadine
    Tribollet, Bernard
    Vivier, Vincent
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2007, 154 (02) : C108 - C113
  • [27] Corrosion and electrochemical behaviors of pure aluminum in novel KOH-ionic liquid-water solutions
    Wang, J. M.
    Wang, J. B.
    Shao, H. B.
    Zeng, X. X.
    Zhang, J. Q.
    Cao, C. N.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2009, 60 (12): : 977 - 981
  • [28] Magnesium-deficient rats prefer magnesium-containing to pure water, but not to sweet tasting solutions
    Classen, HG
    Schimatschek, HF
    Baier, S
    MAGNESIUM-BULLETIN, 1998, 20 (01): : 5 - 7
  • [29] Magnesium-@deficient rats prefer magnesium-@containing to pure water, but not to sweet tasting solutions
    Classen, H. G.
    Schimatschek, H. F.
    Baier, S.
    Magnesium Bulletin/Gesellschaft fuer Magnesium-Forschung, 20 (01):
  • [30] Gibbsite crystal growth in caustic aluminate solutions under different flow regimes
    Li, T
    Bedell, D
    Livk, I
    Ilievski, D
    HYDROMETALLURGY 2003 PROCEEDINGS, VOLS 1 AND 2: VOL 1: LEARNING AND SOLUTION PURIFICATION, 2003, : 1793 - 1802