Improved water resistance and adhesive performance of a commercial UF resin blended with glutaraldehyde

被引：15
作者：
Maminski, ML
Pawlicki, J
Parzuchowski, P
机构：
[1] Agr Univ Warsaw, Fac Wood Technol, PL-02776 Warsaw, Poland
[2] Warsaw Univ Technol, Fac Chem, Warsaw, Poland
来源：
JOURNAL OF ADHESION | 2006年 / 82卷 / 06期
关键词：
adhesives; glutaraldehyde; UF;
D O I：
10.1080/00218460600766731
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The influence of glutaraldehyde blend on the properties of a commercially available resin in moist conditions was investigated. A UF resin with very low water resistance was blended with glutaraldehyde prior to the thermosetting step and the adhesive performance of the modified adhesive systems was studied. Experiments were performed on birch two-layer co-oriented plywood. It was shown that blending a commercial glue-mix as sold with glutaraldehyde can be an effective way to improve water resistance of the glue without introducing additional -NH2 moiety. It was also found that glutaraldehyde does not deteriorate properties of the glue in the dry state, while glue susceptibility to boiling water is markedly reduced.
引用
收藏
页码：629 / 641
页数：13
相关论文
共 17 条
[1]   Preparation and in-vitro evaluation of nifedipine loaded albumin microspheres cross-linked by different glutaraldehyde concentrations [J].
Chuo, WH ;
Tsai, TR ;
Hsu, SH ;
Cham, TM .
INTERNATIONAL JOURNAL OF PHARMACEUTICS, 1996, 144 (02) :241-245
[2]  
Cremonini C., 1997, Holzforschung und Holzverwertung, V49, P11
[3]  
DUNKY M, 2004, CHALLENGES FORMALDEH
[4]   POLYAMINE-MODIFIED UREA-FORMALDEHYDE RESINS .2. RESISTANCE TO STRESS-INDUCED BY MOISTURE CYCLING OF SOLID WOOD JOINTS AND PARTICLEBOARD [J].
EBEWELE, RO ;
RIVER, BH ;
MYERS, GE ;
KOUTSKY, JA .
JOURNAL OF APPLIED POLYMER SCIENCE, 1991, 43 (08) :1483-1490
[5]   BEHAVIOR OF AMINE-MODIFIED UREA FORMALDEHYDE-BONDED WOOD JOINTS AT LOW FORMALDEHYDE UREA MOLAR RATIOS [J].
EBEWELE, RO ;
RIVER, BH ;
MYERS, GE .
JOURNAL OF APPLIED POLYMER SCIENCE, 1994, 52 (05) :689-700
[6]  
Fleischer O, 2000, HOLZ ROH WERKST, V58, P295, DOI 10.1007/s001070050431
[7]  
FREEMAN HG, 1968, FOREST PROD J, V7, P39
[8]  
GLAZKOV SS, 1997, DEREVOOBRABATYVAYUSH, V4, P15
[9]   Biocompatibility studies of anionic collagen membranes with different degree of glutaraldehyde cross-linking [J].
Goissis, G ;
Junior, EM ;
Marcantônio, JAC ;
Lia, RCC ;
Cancian, DCJ ;
de Carvalho, M .
BIOMATERIALS, 1999, 20 (01) :27-34
[10]   Reaction of poly(vinyl alcohol) and dialdehydes during gel formation probed by H-1 nmr - A kinetic study [J].
Hansen, EW ;
Holm, KH ;
Jahr, DM ;
Olafsen, K ;
Stori, A .
POLYMER, 1997, 38 (19) :4863-4871
12