Synthesis and Characterization of Styrene, Maleic Anhydride and N-phenyl Maleimide Tripolymer

被引：0

作者：

Mou, Y. L. ^{[1
]}

Xia, W. ^{[1
]}

Wang, Z. ^{[1
]}

Zheng, D. F. ^{[1
]}

机构：

[1] Hainan Inst Sci & Technol, Sch Biochem Chem Engn, Haikou 571100, Peoples R China

来源：

PROCEEDINGS OF THE 2ND ANNUAL INTERNATIONAL CONFERENCE ON ADVANCED MATERIAL ENGINEERING (AME 2016) | 2016年 / 85卷

关键词：

Terpolymer; characterization; thermal resistance; DSC/TG test; COPOLYMERIZATION;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A terpolymer resin (NSMA) was synthesized with styrene, maleic anhydride and N-phenyl maleimide. The structure and composition was characterized with FT-IR and C-13-NMR. The thermal resistance of NSMA was determined through integrated thermal analysis. The results indicated that, when the molar ratio of N-PMI, St and MA was 1:3:1, the T-g, T-wt10%, T-wt20%, T-wt50%, and T-max of NSMA was 227 degrees C, 394 degrees C, 409 degrees C, 431 degrees C and 434 degrees C, respectively, much higher than those of styrene/maleic anhydride copolymer. Furthermore, the thermal resistance of NSMA increased with the content of N-phenyl maleimide. The results showed that NSMA had a favorable application prospect in the thermal resistance resin.

引用

页码：1110 / 1115

页数：6

共 13 条

[1] N-phenylmaleimide polymers for second-order nonlinear optics [J].

Chang, JY ;

Kim, TJ ;

Han, MJ ;

Choi, DH ;

Kim, N .

POLYMER, 1997, 38 (18) :4651-4656

[2] Effect of comonomer composition on the controlled free-radical copolymerization of styrene and maleic anhydride by reversible addition-fragmentation chain transfer (RAFT) [J].

Chernikova, E ;

Terpugova, P ;

Bui, CO ;

Charleux, B .

POLYMER, 2003, 44 (15) :4101-4107

[3] Preparation and characterization of epoxy-cyanate ester interpenetrating network matrices/organoclay nanocomposites [J].

Dinakaran, K ;

Alagar, M .

POLYMERS FOR ADVANCED TECHNOLOGIES, 2003, 14 (08) :574-585

[4]

Liang G.Z., 2004, CN Patent, Patent No. [1,493,600, 1493600]

[5] Synthesis of novel trifunctional epoxy resins and their modification with polydimethylsiloxane for electronic application [J].

Lin, LL ;

Ho, TH ;

Wang, CS .

POLYMER, 1997, 38 (08) :1997-2003

[6]

Shen N.X., 1997, MATER SCI ENG, V13, P39

[7]

Suzuki K., 2006, JP Patent, Patent No. [8,134,328, 8134328]

[8] Preparation and characterization of polyester based on bis-(2-hydroxypropyl terephthalate) [J].

Tawfik, ME ;

Elsabee, MZ .

JOURNAL OF POLYMER RESEARCH-TAIWAN, 2002, 9 (02) :129-133

[9]

Teraki S., 2009, JP Patent, Patent No. [2,009,111,276, 2009111276]

[10]

Thamizharasi S, 2001, J APPL POLYM SCI, V80, P1870, DOI 10.1002/app.1284

← 1 2 →