Effects of the aging time and temperature on the microstructures and mechanical properties of 6082 aluminum alloy extrusions

被引：1

作者：

Wu, Tao ^{[1
]}

Ding, Xianfei ^{[1
]}

Sun, Jing

Zhang, Weidong ^{[1
]}

Sun, Dongbai ^{[1
]}

Wang, Lichen

机构：

[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China

来源：

ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3 | 2013年 / 652-654卷

关键词：

6082 aluminum alloy; aging; microstructure; mechanical properties;

D O I：

10.4028/www.scientific.net/AMR.652-654.1035

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The main task of this work was to study the effects of aging time and aging temperature on the microstructure and mechanical properties of 6082 aluminum alloy extrusions. Artificial aging was performed on the alloy extrusions at the temperatures of 150, 175 and 200 degrees C for the aging times of 4, 8 and 12 h. The microstructure evolution of the aluminum alloy extrusions with increase of the aging time and temperature was investigated by Field Emission Scanning Electron Microscope (FESEM). For the purpose of how the aging process affected the mechanical properties, tensile tests were performed. The results showed that the optimum aging treatment was 175 degrees C/4 h. Under this condition, the tensile strength (Rm) and the yield strength (Rp) in the longitudinal direction of the extrusions reached the maximum value more than 350MPa and 320MPa, respectively, and the tensile elongation (A) was more than 15%.

引用

页码：1035 / 1042

页数：8

共 12 条

[1]

Chen Hui, 2007, ALUMINUM FABRICATION, V6, P25

[2]

Chen J.G., 2010, METALLIC FUNCT MAT, V17, P16

[3] The precipitation sequence in Al-Mg-Si alloys [J].

Edwards, GA ;

Stiller, K ;

Dunlop, GL ;

Couper, MJ .

ACTA MATERIALIA, 1998, 46 (11) :3893-3904

[4]

Jin Man, 2007, 9 HEAT TREATM GEN AS, V9, P160

[5]

Jun Luo, 2007, METALLURGICAL COLLEC, V4, P4

[6]

Lizi He, 2001, MICROSTRUCTURES MECH

[7] An investigation into the mechanical and tribological properties of plasma electrolytic oxidation and hard-anodized coatings on 6082 aluminum alloy [J].

Malayoglu, Ugur ;

Tekin, Kadir C. ;

Malayoglu, Ufuk ;

Shrestha, Suman .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (24) :7451-7460

[8] Influence of heat treatment on the microstructure and mechanical properties of 6005 and 6082 aluminium alloys [J].

Mrówka-Nowotnik, G ;

Sieniawski, J .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2005, 162 :367-372

[9] Study on the fatigue strength of AA 6082-T6 adhesive lap joints [J].

Pereira, A. M. ;

Ferreira, J. M. ;

Antunes, F. V. ;

Bartolo, P. J. .

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2009, 29 (06) :633-638

[10]

Wang Y.J., 2004, WELDING, V10, P5

← 1 2 →