Contact angles of liquid metals on quasicrystals

Wetting with mu m-sized Pb droplets on thin polycrystalline films of decagonal Al13Co4 is reported. The films were prepared under high vacuum conditions in order to have Pb droplets lying on a clean surface. The method used is sequential deposition and annealing of specific stackings of Al and Co layers of nanometric thicknesses. A 300 nm thick Pb slab was then deposited on top of the films and dewetting experiments were followed in situ in a scanning Auger microprobe. The contact angle between the Pb droplet and the surface of the film is measured to be 49 degrees +/- 7 degrees. Further investigation performed by cross section transmission electron microscopy allows us to better characterize the interface. Taking into account the rugosity of the film, it is concluded that there is partial wetting of the film, which corresponds to a smaller contact angle. The comparison with other results obtained either with pure metals or with a cubic AlCo compound leads to the conclusion that the wetting behaviour of Pb on the surface of a decagonal compound is close to that of a metal with a high melting point and not significantly different from that of a crystalline compound with a small unit cell.