Investigation of crack initiation and propagation behavior of AISI 310 stainless steel up to very high cycle fatigue

被引：14
|
作者：
Khan, M. K. [1 ]
Wang, Q. Y. [1 ]
机构：
[1] Sichuan Univ, Dept Mech & Engn Sci, Chengdu 610065, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2013年 / 54卷
基金：
中国国家自然科学基金;
关键词：
Very high cycle fatigue; Surface roughness; PSBs; Local plasticity; Crack initiation; GIGACYCLE FATIGUE; SURFACE-RELIEF; BEARING STEEL; MECHANISM; IRON; AFM;
D O I：
10.1016/j.ijfatigue.2013.04.009
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fatigue behavior up to very high cycles for AISI 310 stainless steel has been investigated. The fatigue crack initiated from the surface of the material. It was found that up to 10(6) cycles, cracks initiated from the carbide precipitates at grain boundaries. However, above 10(6) cycles, the cracks initiated from persistent slip bands found at the surface of the specimen. At lower stress levels, slip bands were developed without initiating the cracks. The horizontal asymptote S-N curve from 10(6) to 10(9) cycles was attributed to the development of slip bands all over the surface of the specimen, before crack initiation. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：38 / 46
页数：9
相关论文
共 50 条
  • [41] Fretting behaviors of a steel up to very high cycle fatigue
    Teng, Zhenjie
    Liu, Hanqing
    Wang, Qingyuan
    Huang, Zhiyong
    Starke, Peter
    WEAR, 2019, 438
  • [42] Fatigue crack initiation site transition of high-strength steel under very high-cycle fatigue
    Teng, Xiaoyuan
    Pang, Jianchao
    Gao, Chong
    Li, Shouxin
    Zhang, Zhefeng
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (12) : 4450 - 4464
  • [43] High and very high cycle fatigue behavior of an additive manufactured hot-work tool steel
    Chantziara, Katerina
    Nikas, Dimitrios
    Bergstrom, Jens
    Grehk, Mikael
    Pappa, Maria
    Michailidis, Nikolaos
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2024, 917
  • [44] Very High Cycle Fatigue Behavior of Austenitic Stainless Steel in Annealed and Predeformed Condition
    Sarkar, Aritra
    Klusak, Jan
    Kozakova, Kamila
    Christ, H. -j.
    MATERIALS PERFORMANCE AND CHARACTERIZATION, 2023, 12 (02) : 78 - 92
  • [45] Micro-crack initiation and propagation in a high strength aluminum alloy during very high cycle fatigue
    Xu, Luopeng
    Wang, Qingyuan
    Zhou, Min
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 715 : 404 - 413
  • [46] Very-high-cycle fatigue behavior of a structural steel with and without induced surface defects
    Jiang, Qingqing
    Sun, Chengqi
    Liu, Xiaolong
    Hong, Youshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 93 : 352 - 362
  • [47] Effect of Artificial Defects on the Very High Cycle Fatigue Behavior of 316L Stainless Steel
    Xiong, Zhihong
    Naoe, Takashi
    Futakawa, Masatoshi
    METALS, 2019, 9 (04):
  • [48] Very high cycle fatigue behavior of bearing steel with rare earth addition
    Yang, Chaoyun
    Luan, Yikun
    Li, Dianzhong
    Li, Yiyi
    Tariq, Naeem ul Haq
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 131 (131)
  • [49] The role of local plasticity during very high cycle fatigue crack initiation in high-strength steels
    Spriestersbach, D.
    Kerscher, E.
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 111 : 93 - 100
  • [50] Non-inclusion induced crack initiation in multiphase high-strength steel during very high cycle fatigue
    Zhao, P.
    Liu, Z.
    Misra, R. D. K.
    Du, F.
    Zhang, C.
    Yang, Z. G.
    Yan, E.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 712 : 406 - 413
12345