Investigation of crack initiation and propagation behavior of AISI 310 stainless steel up to very high cycle fatigue

被引：14
|
作者：
Khan, M. K. [1 ]
Wang, Q. Y. [1 ]
机构：
[1] Sichuan Univ, Dept Mech & Engn Sci, Chengdu 610065, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2013年 / 54卷
基金：
中国国家自然科学基金;
关键词：
Very high cycle fatigue; Surface roughness; PSBs; Local plasticity; Crack initiation; GIGACYCLE FATIGUE; SURFACE-RELIEF; BEARING STEEL; MECHANISM; IRON; AFM;
D O I：
10.1016/j.ijfatigue.2013.04.009
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fatigue behavior up to very high cycles for AISI 310 stainless steel has been investigated. The fatigue crack initiated from the surface of the material. It was found that up to 10(6) cycles, cracks initiated from the carbide precipitates at grain boundaries. However, above 10(6) cycles, the cracks initiated from persistent slip bands found at the surface of the specimen. At lower stress levels, slip bands were developed without initiating the cracks. The horizontal asymptote S-N curve from 10(6) to 10(9) cycles was attributed to the development of slip bands all over the surface of the specimen, before crack initiation. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：38 / 46
页数：9
相关论文
共 50 条
  • [31] Very high cycle fatigue of cold rolled stainless steels, crack initiation and formation of the fine granular area
    Tofique, Muhammad Waqas
    Bergstrom, Jens
    Svensson, Krister
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 100 : 238 - 250
  • [32] High-cycle and very-high-cycle fatigue behavior of a stainless steel for air-conditioning compressor valve plates
    Jia, Xu
    Xiang, Yang Ou
    Pei, Hu Yuan
    Wei, Song
    INTERNATIONAL JOURNAL OF STRUCTURAL INTEGRITY, 2022, 13 (02) : 185 - 195
  • [33] Very high cycle fatigue behavior of dissimilar martensitic stainless-steel diffusion-bonded joints
    Nie, Baohua
    Zhao, Zihua
    Chen, Dongchu
    Liu, Fangjun
    Zhao, Jishi
    Zhao, Lianyu
    MATERIALS EXPRESS, 2019, 9 (09) : 1120 - 1126
  • [34] Investigation of crack initiation mechanisms responsible for the fish eye formation in the Very High Cycle Fatigue regime
    Wang, Chong
    Petit, Johann
    Huang, Zhiyong
    Wagner, Daniele
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 119 (320-329) : 320 - 329
  • [35] Very-high-cycle fatigue crack initiation and propagation behaviours of magnesium alloy ZK60
    He, Chao
    Liu, Yongjie
    Li, Jiukai
    Yang, Kun
    Wang, Qingyuan
    Chen, Qiang
    MATERIALS SCIENCE AND TECHNOLOGY, 2018, 34 (06) : 639 - 647
  • [36] Characterization on Crack Initiation and Early Propagation Region of Nickel-Based Alloys in Very High Cycle Fatigue
    Chen, Zelin
    Dong, Zihao
    Liu, Chang
    Dai, Yajun
    He, Chao
    MATERIALS, 2022, 15 (17)
  • [37] Study of Fatigue Crack Initiation in 316 Stainless Steel
    Benabdeljalil, O.
    Khan, M. K.
    Fitzpatrick, M. E.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2025, 48 (04) : 1893 - 1904
  • [38] High-Cycle Fatigue Properties and Crack Initiation and Propagation Behavior of 2397 Alloy
    Fan Xuesong
    Zheng Ziqiao
    Zhang Long
    Hu Fang
    Gong Zhu
    RARE METAL MATERIALS AND ENGINEERING, 2017, 46 (05) : 1327 - 1333
  • [39] Relationship between non-inclusion induced crack initiation and microstructure on fatigue behavior of bainite/martensite steel in high cycle fatigue/very high cycle (HCF/VHCF) regime
    Gui, Xiaolu
    Gao, Guhui
    An, Baifeng
    Misra, R. D. K.
    Bai, Bingzhe
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 803
  • [40] Micro-mechanism associated with very high cycle fatigue crack initiation of advanced DQ&P processed steel
    Ghosh, Sumit
    Schoenbauer, Bernd M.
    Pallaspuro, Sakari
    Somani, Mahesh
    Mayer, Herwig
    Koemi, Jukka
    23 EUROPEAN CONFERENCE ON FRACTURE, ECF23, 2022, 42 : 919 - 926
12345