Consolidation and properties of ultrafine binderless cemented carbide by spark plasma sintering

被引:9
作者
Liu Xiangqing [1 ]
Lin Tao [1 ]
Shao Huiping [1 ]
Guo Zhimeng [1 ]
Luo Ji [1 ]
Hao Junjie [1 ]
机构
[1] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
关键词
cemented carbide; binderless carbide; ultrafine; mechanical properties; spark plasma sintering;
D O I
10.1016/S1001-0521(08)60137-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Owing to the absence of metal binder, binderless cemented carbides have higher wear, corrosion, and oxidation resistance. WC-0.3VC0.5Cr(3)C(2) powders with an average particle size of 200 nm and a little amount of active element were consolidated by spark plasma sintering. The sintered microstructure revealed that the average WC grain size was 0.24 mu m, which was almost consistent with the initial fine powder. The results of XRD showed that W2C phase was formed. Nearly complete densification of ultrafine binderless cemented carbide was achieved by sintering at 1400 degrees C for 120 s under 50 MPa. The resulting hardness and the fracture toughness were 28.18 GPa and 6.05 MPa.m(1/2), respectively.
引用
收藏
页码:320 / 323
页数:4
相关论文
共 5 条
[1]   A CRITICAL-EVALUATION OF INDENTATION TECHNIQUES FOR MEASURING FRACTURE-TOUGHNESS .1. DIRECT CRACK MEASUREMENTS [J].
ANSTIS, GR ;
CHANTIKUL, P ;
LAWN, BR ;
MARSHALL, DB .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (09) :533-538
[2]   Microstructures of binderless tungsten carbides sintered by spark plasma sintering process [J].
Cha, SI ;
Hong, SH .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2) :381-389
[3]   Bulk ultrafine binderless WC prepared by spark plasma sintering [J].
Huang, B ;
Chen, LD ;
Bai, SQ .
SCRIPTA MATERIALIA, 2006, 54 (03) :441-445
[4]   Consolidation and properties of binderless sub-micron tungsten carbide by field-activated sintering [J].
Kim, HC ;
Shon, IJ ;
Garay, JE ;
Munir, ZA .
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2004, 22 (06) :257-264
[5]   Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS) [J].
Omori, M .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 287 (02) :183-188