Thermoluminescence of chemical vapor deposited diamond film

被引:1
|
作者
Kim, T [1 ]
机构
[1] Chonju Natl Univ Educ, Dept Sci Educ, Chonju 560757, South Korea
来源
RADIATION EFFECTS AND DEFECTS IN SOLIDS | 2001年 / 156卷 / 1-4期
关键词
chemical vapor deposited diamond film; thermoluminescence; defect;
D O I
10.1080/10420150108216895
中图分类号
TL [原子能技术]; O571 [原子核物理学];
学科分类号
0827 ; 082701 ;
摘要
Diamond films were synthesized by a chemical vapor deposition (CVD). Raman spectrum showed the diamond line at 1332 cm(-1) and X-ray diffraction pattern exhibited a strong (111) peak of diamond. The scanning electron microscopy analysis showed that the CVD diamond film was grown to be unepitaxial crystallites with pyramidal hillocks. Three-dimensional thermoluminescence spectrum of CVD diamond film irradiated with X-ray produced one peak at 560 K and 430 nm. The main 560 K glow curve was caused by first order kinetics. Activation energy, and escape frequency of the main peak were calculated to be 0.92similar to1.05 eV and 3.4 x 10(7) s(-1) respectively. The emission spectrum at 560 K was split into 1.63 eV, 2.60 eV, and 3.07 eV emission bands that were found to be associated with silicon-vacancy center, H3, and A center, respectively.
引用
收藏
页码:209 / 214
页数:6
相关论文
共 50 条
  • [31] Electron field emission from chemical vapor deposited diamond
    Zhu, W
    Kochanski, GP
    Jin, S
    Seibles, L
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 1996, 14 (03): : 2011 - 2019
  • [32] Characterization of chlorinated chemical vapor deposited and natural (100) diamond
    Chaney, JA
    Feigerle, CS
    SURFACE SCIENCE, 1999, 425 (2-3) : 245 - 258
  • [33] SI IMPURITY IN CHEMICAL VAPOR-DEPOSITED DIAMOND FILMS
    RUAN, J
    CHOYKE, WJ
    PARTLOW, WD
    APPLIED PHYSICS LETTERS, 1991, 58 (03) : 295 - 297
  • [34] Optical excitation of paramagnetic nitrogen in chemical vapor deposited diamond
    Graeff, CFO
    Rohrer, E
    Nebel, CE
    Stutzmann, M
    Guttler, H
    Zachai, R
    APPLIED PHYSICS LETTERS, 1996, 69 (21) : 3215 - 3217
  • [36] Local thermal conductivity in chemical-vapor-deposited diamond
    Graebner, J.E., 1600, American Inst of Physics, Woodbury, NY, United States (76):
  • [37] A study of substitutional nitrogen impurities in chemical vapor deposited diamond
    Sitch, PK
    Jungnickel, G
    Kaukonen, M
    Porezag, D
    Frauenheim, T
    Pederson, MR
    Jackson, KA
    JOURNAL OF APPLIED PHYSICS, 1998, 83 (09) : 4642 - 4646
  • [38] Characterization of chlorinated chemical vapor deposited and natural (100) diamond
    Chaney, J.A.
    Feigerle, C.S.
    Surface Science, 1999, 425 (02): : 245 - 258
  • [39] CATHODOLUMINESCENCE AND PHOTOLUMINESCENCE FROM CHEMICAL-VAPOR-DEPOSITED DIAMOND
    YANG, XX
    BARNES, AV
    ALBERT, MM
    ALBRIDGE, RG
    MCKINLEY, JT
    TOLK, NH
    DAVIDSON, JL
    JOURNAL OF APPLIED PHYSICS, 1995, 77 (04) : 1758 - 1761