VHCF behaviour of case-hardened specimens made of two grades of steel SAE 5120 differing in microstructure

被引:10
作者
Bomas, Hubert [1 ]
Burkart, Klaus [1 ]
Zoch, Hans-Werner [1 ]
机构
[1] Stiftung Inst Werkstofftech IWT, D-28359 Bremen, Germany
关键词
Case-hardened steel; Crack initiation; Very high cycle fatigue (VHCF); Kitagawa diagram; Competing sites of crack initiation; CYCLE MULTIAXIAL FATIGUE; WEAKEST-LINK CONCEPT; ENDURANCE LIMIT; LIFE; COMPONENTS; GRADIENT; DESIGN; VOLUME; SIZE;
D O I
10.1016/j.ijfatigue.2012.10.001
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
In this investigation notched and fracture mechanics specimens were machined from the steel SAE 5120 (DIN EN 20MnCr5) in two cleanliness conditions. The first material is used for high-performance components and is nearly free of oxides. The second material is standard steel and used for common requests in the field of drive engineering containing non-metallic inclusions in a dimension that is state of the art in steel making. The notched specimens were case-hardened in two different ways. Afterwards, the surfaces were ground and therefore showed compressive residual stresses. Uniaxial VHCF tests were performed up to 200 million cycles under the stress ratios R = -1 and R = 0 using two resonant pulse systems. For this purpose the geometries of the specimens had been optimised so that the achieved test frequency was 190 Hz. Fatigue failure is possible at all applied numbers of cycles meaning that there is no real fatigue limit in this region. Fatigue crack initiation took place from different origins and at different sites. Different analyses are shown for interpretating the type of fatigue crack initiation and its site in the specimen. The fracture mechanics specimens were blank hardened in order to have the core properties of the notched specimens. Crack propagation was measured in the near-threshold region. An extended Kitagawa diagram is shown to demonstrate the influence of stress amplitude and flaw size on the failure probability. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码:63 / 73
页数:11
相关论文
共 34 条
[1]  
[Anonymous], BETRIEBSFESTIGKEIT
[2]  
[Anonymous], 1995, E64795A ASTM
[3]   Material aspects and design methods for high-pressure-components of hard steels subject to cyclical loads [J].
Bacher-Höchst, M ;
Linkewitz, T ;
Mühleder, F .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2002, 25 (12) :1169-1173
[4]  
Basquin O. H., 1910, Proc Am Soc Test Mater, V10, P625
[5]   Failure mechanisms of automotive metallic alloys in very high cycle fatigue range [J].
Bayraktar, Emin ;
Garcias, Israel Marines ;
Bathias, Claude .
INTERNATIONAL JOURNAL OF FATIGUE, 2006, 28 (11) :1590-1602
[6]  
Bohm J, 1982, Materwiss Werksttech, V13, P120, DOI [10.1002/mawe.19820130408, DOI 10.1002/MAWE.19820130408]
[7]   Application of the weakest-link concept to the endurance limit of notched and multiaxially loaded specimens of carburized steel 16MnCrS5 [J].
Bomas, H ;
Schleicher, M .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2005, 28 (11) :983-995
[8]   Calculation method for the fatigue limit of parts of case hardened steels [J].
Bomas, H ;
Mayr, P ;
Schleicher, M .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 234 :393-396
[9]   Crack initiation and endurance limit of a hard steel under multiaxial cyclic loads [J].
Bomas, H. ;
Bacher-Hoechst, M. ;
Kienzler, R. ;
Kunow, S. ;
Loewisch, G. ;
Muehleder, F. ;
Schroeder, R. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2010, 33 (02) :126-139
[10]   Application of a weakest-link concept to the fatigue limit of the bearing steel SAE 52100 in a bainitic condition [J].
Bomas, H ;
Linkewitz, T ;
Mayr, P .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1999, 22 (09) :733-741