Microstructure and mechanical properties of double continuously extruded Mg-Zn-Gd-based magnesium alloys

被引:28
作者
Huang, Hua [1 ]
Yuan, Guangyin [1 ,2 ]
Chu, Zhenhua [1 ]
Ding, Wenjiang [1 ,2 ]
机构
[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Shanghai 200240, Peoples R China
[2] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composite, Shanghai 200240, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 560卷
基金
高等学校博士学科点专项科研基金;
关键词
Magnesium; DCE; Microstructure; Mechanical properties; Strengthening; QUASI-CRYSTALLINE PHASE; FRACTURE-TOUGHNESS; ICOSAHEDRAL PHASE; GRAIN-REFINEMENT; Y ALLOYS; EXTRUSION; STRENGTH; AL; DISPERSION; PARTICLES;
D O I
10.1016/j.msea.2012.09.063
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Double continuous extrusion (DCE) is proposed here as a novel thermomechanical process which means that the sample is continuously extruded twice by one process. The microstructures and mechanical properties of Mg98Zn1.92Gd0.08 (at%, Alloy 1) and Mg96.83Zn2.7Gd0.47 (at%, Alloy 2) after conventional extrusion and DCE at 373 K were investigated. The results show that the major secondary phase in Alloy 1 is Mg2Zn3 and that in Alloy 2 is icosahedral quasicrystals phase (I-phase). After DCE, the microstructure is refined, and the average grain sizes of the both alloys are smaller than 1 mu m, and this further improves the mechanical properties. Both the alloys exhibit excellent mechanical properties, and the ultimate tensile strength, yield strength and elongation to failure are 434 MPa, 410 MPa and 14.6%, respectively, for Alloy 1; and 444 MPa, 417 MPa and 13.1%, respectively, for Alloy 2. The possible strengthening mechanisms were discussed and it was found that DCE is an effective method for Mg-based alloys strengthening by grain refinement and secondary phase dispersion. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码:241 / 248
页数:8
相关论文
共 30 条
[1]   PLASTIC DEFORMATION OF POLYCRYSTALLINE AGGREGATES [J].
ARMSTRONG, R ;
DOUTHWAITE, RM ;
CODD, I ;
PETCH, NJ .
PHILOSOPHICAL MAGAZINE, 1962, 7 (73) :45-&
[2]  
Ashby M.F., 1982, DEFORMATION MECH MAP
[3]   Texture evolution in equal-channel angular extrusion [J].
Beyerlein, Irene J. ;
Toth, Laszlo S. .
PROGRESS IN MATERIALS SCIENCE, 2009, 54 (04) :427-510
[4]   TRANSMISSION ELECTRON MICROSCOPY STUDY OF AGE HARDENING IN A MG-5 WT PER CENT ZN ALLOY [J].
CLARK, JB .
ACTA METALLURGICA, 1965, 13 (12) :1281-&
[5]   Improvement of strength of magnesium alloy processed by equal channel angular extrusion [J].
Ding, S. X. ;
Lee, W. T. ;
Chang, C. P. ;
Chang, L. W. ;
Kao, P. W. .
SCRIPTA MATERIALIA, 2008, 59 (09) :1006-1009
[6]   INDEXING PROBLEMS IN QUASICRYSTAL DIFFRACTION [J].
ELSER, V .
PHYSICAL REVIEW B, 1985, 32 (08) :4892-4898
[7]   Solid solution strengthening behaviors in binary Mg-Y single phase alloys [J].
Gao, L. ;
Chen, R. S. ;
Han, E. H. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 472 (1-2) :234-240
[8]   THE AL-CU-FE PHASE-DIAGRAM - 0 TO 25 AT-PCT FE AND 50 TO 75 AT-PCT AL - EQUILIBRIA INVOLVING THE ICOSAHEDRAL PHASE [J].
GAYLE, FW ;
SHAPIRO, AJ ;
BIANCANIELLO, FS ;
BOETTINGER, WJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (09) :2409-2417
[9]   Microstructures and mechanical properties of double hot-extruded AZ80+xSr wrought alloys [J].
Guan Shao-Kang ;
Zhu Shi-Jie ;
Wang Li-Guo ;
Yang Qing ;
Cao Wen-Bo .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 (06) :1143-1151
[10]   Microstructure and mechanical properties of Mg-Al-Zn alloy deformed by cold extrusion [J].
Liang, S. J. ;
Liu, Z. Y. ;
Wang, E. D. .
MATERIALS LETTERS, 2008, 62 (17-18) :3051-3054