Hot tensile deformation behavior of Mg-Zn-Al magnesium alloy tubes processed by severe plastic deformation

被引:35
作者
Eftekhari, M. [1 ]
Fata, A. [2 ]
Faraji, G. [1 ]
Mashhadi, M. M. [1 ]
机构
[1] Univ Tehran, Coll Engn, Sch Mech Engn, Tehran 111554563, Iran
[2] Univ Hormozgan, Dept Mech Engn, Fac Engn, Hormozgan, Iran
关键词
PTCAP; AZ31; alloy; Hot deformation; Severe plastic deformation; Ultra-fine grained; HIGH-TEMPERATURE DEFORMATION; HIGH-PRESSURE TORSION; ANGULAR PRESSING PTCAP; GRAIN-REFINEMENT; MICROSTRUCTURAL INSTABILITY; DYNAMIC RECRYSTALLIZATION; SUPERPLASTIC DEFORMATION; ELEVATED-TEMPERATURES; MECHANICAL-PROPERTIES; CYLINDRICAL-TUBES;
D O I
10.1016/j.jallcom.2018.01.246
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In the current study, parallel tubular channel angular pressing (PTCAP), as a severe plastic deformation (SPD) method, was applied on a commercial pre extruded Mg-3Al-1Zn (AZ31) alloy tubes at 300 degrees C to achieve a fine-grained (FG) structure. To study the deformation behavior, tensile testing at different temperatures of 25 degrees C, 350 degrees C, 400 degrees C, and 450 degrees C was done on the samples processed by multi-pass PTCAP. Also, the strain rate sensitivity exponent (m) is measured for the four-pass PTCAP processed tube, at 350 degrees C, 400 degrees C and 450 degrees C and strain rates of 10(-2), 10(-3) and 10(-4) 1/s. The average value of m coefficients was similar to 0.3. A higher elongation to failure of similar to 281% was achieved at a higher temperature of 450 degrees C and a lower strain rate of 10(-4) 1/s, due to grain boundary sliding as a dominant deformation mechanism. After the first pass of PTCAP a bimodal microstructure, with large gains surrounded by many small ones, was observed. The grain refinement and homogeneity of the microstructure was enhanced by applying subsequent passes of PTCAP. Vickers microhardness measurements show that by more grain refinement caused by applying for more PTCAP passes, the value of hardness increased. Fractographic SEM images revealed that predominately ductile fracture occurred in all evaluated samples. (c) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码:442 / 453
页数:12
相关论文
共 52 条
[1]   A novel combined severe plastic deformation method for producing thin-walled ultrafine grained cylindrical tubes [J].
Abdolvand, H. ;
Sohrabi, H. ;
Faraji, G. ;
Yusof, F. .
MATERIALS LETTERS, 2015, 143 :167-171
[2]   Mechanical characteristics of superplastic deformation of AZ31 magnesium alloy [J].
Abu-Farha, Fadi K. ;
Khraisheh, Marwan K. .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2007, 16 (02) :192-199
[3]   Analysis of superplastic deformation of AZ31 magnesium alloy [J].
Abu-Farha, Fadi K. ;
Khraisheh, Marwan K. .
ADVANCED ENGINEERING MATERIALS, 2007, 9 (09) :777-783
[4]   Dynamic recrystallization during high temperature deformation of magnesium [J].
Al-Samman, T. ;
Gottstein, G. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 490 (1-2) :411-420
[5]   Structural and hardness inhomogeneities in Mg-Al-Zn alloys processed by high-pressure torsion [J].
Al-Zubaydi, Ahmed ;
Figueiredo, Roberto B. ;
Huang, Yi ;
Langdon, Terence G. .
JOURNAL OF MATERIALS SCIENCE, 2013, 48 (13) :4661-4670
[6]   Microstructure and hardness inhomogeneity of fine-grained AM60 magnesium alloy subjected to cyclic expansion extrusion (CEE) [J].
Amani, S. ;
Faraji, G. ;
Abrinia, K. .
JOURNAL OF MANUFACTURING PROCESSES, 2017, 28 :197-208
[7]   Microstructure, texture and mechanical properties of aluminum processed by high-pressure tube twisting [J].
Arzaghi, M. ;
Fundenberger, J. J. ;
Toth, L. S. ;
Arruffat, R. ;
Faure, L. ;
Beausir, B. ;
Sauvage, X. .
ACTA MATERIALIA, 2012, 60 (11) :4393-4408
[8]   Effect of temperature, strain rate and fibre orientation on the plastic flow behaviour and formability of AZ31 magnesium alloy [J].
Bruni, C. ;
Forcellese, A. ;
Gabrielli, F. ;
Simoncini, M. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2010, 210 (10) :1354-1363
[9]   Hot tensile deformation behavior and microstructural evolution of a Mg-9.3Li-1.79Al-1.61Zn alloy [J].
Cao, Furong ;
Xia, Fei ;
Xue, Guoqiang .
MATERIALS & DESIGN, 2016, 92 :44-57
[10]   Hot tensile deformation and fracture behaviors of AZ31 magnesium alloy [J].
Deng, Jiao ;
Lin, Y. C. ;
Li, Shui-Sheng ;
Chen, Jian ;
Ding, Yi .
MATERIALS & DESIGN, 2013, 49 :209-219