Effects of Surface Treatments, Thermocycling, and Cyclic Loading on the Bond Strength of a Resin Cement Bonded to a Lithium Disilicate Glass Ceramic

被引:98
作者
Guarda, G. B. [1 ]
Correr, A. B. [1 ]
Goncalves, L. S. [1 ]
Costa, A. R. [1 ]
Borges, G. A. [1 ]
Sinhoreti, M. A. C. [1 ]
Correr-Sobrinho, L. [1 ]
机构
[1] State Univ Campinas UNICAMP, Piracicaba Dent Sch, Dept Restorat Dent, Dent Mat Div, Piracicaba, SP, Brazil
关键词
PORCELAIN REPAIR SYSTEMS; LUTING CEMENT; COMPOSITE RESIN; DURABILITY; ADHESION; STORAGE; CROWNS; AGENTS;
D O I
10.2341/11-076-L
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
Objectives: The aim of this present study was to investigate the effect of two surface treatments, fatigue and thermocycling, on the microtensile bond strength of a newly introduced lithium disilicate glass ceramic (IPS e.max Press, Ivoclar Vivadent) and a dual-cured resin cement. Methods: A total of 18 ceramic blocks (10 mm long X 7 mm wide X 3.0 mm thick) were fabricated and divided into six groups (n=3): groups 1, 2, and 3-air particle abraded for five seconds with 50-mu m aluminum oxide particles; groups 4, 5, and 6-acid etched with 10% hydrofluoric acid for 20 seconds. A silane coupling agent was applied onto all specimens and allowed to dry for five seconds, and the ceramic blocks were bonded to a block of composite Tetric N-Ceram (Ivoclar Vivadent) with RelyX ARC (3M ESPE) resin cement and placed under a 500-g static load for two minutes. The cement excess was removed with a disposable microbrush, and four periods of light activation for 40 seconds each were performed at right angles using an LED curing unit (UltraLume LED 5, Ultradent) with a final 40 second light exposure from the top surface. All of the specimens were stored in distilled water at 37 degrees C for 24 hours. Groups 2 and 5 were submitted to 3,000 thermal cycles between 5 degrees C and 55 degrees C, and groups 3 and 6 were submitted to a fatigue test of 100,000 cycles at 2 Hz. Specimens were sectioned perpendicular to the bonding area to obtain beams with a cross-sectional area of 1 mm(2) (30 beams per group) and submitted to a microtensile bond strength test in a testing machine (EZ Test) at a cross-head speed of 0.5 mm/min. Data were submitted to analysis of variance and Tukey post hoc test (p <= 0.05). Results: The microtensile bond strength values (MPa) were 26.9 +/- 6.9, 22.2 +/- 7.8, and 21.2 +/- 9.1 for groups 1-3 and 35.0 +/- 9.6, 24.3 +/- 8.9, and 23.9 +/- 6.3 for groups 4-6. For the control group, fatigue testing and thermocycling produced a predominance of adhesive failures. Fatigue and thermocycling significantly decreased the microtensile bond strength for both ceramic surface treatments when compared with the control groups. Etching with 10% hydrofluoric acid significantly increased the microtensile bond strength for the control group.
引用
收藏
页码:208 / 217
页数:10
相关论文
共 41 条
[1]  
Anusavice K J., 1996, Philips Science of dental materials, V10th
[2]   BOND STRENGTH OF COMPOSITE RESIN TO PORCELAIN WITH NEWER GENERATION PORCELAIN REPAIR SYSTEMS [J].
APPELDOORN, RE ;
WILWERDING, TM ;
BARKMEIER, WW .
JOURNAL OF PROSTHETIC DENTISTRY, 1993, 70 (01) :6-11
[3]   Influence of surface treatment and cyclic loading on the durability of repaired all-ceramic crowns [J].
Attia, Ahmed .
JOURNAL OF APPLIED ORAL SCIENCE, 2010, 18 (02) :194-200
[4]   Effect of surface treatment on roughness and bond strength of a heat-pressed ceramic [J].
Ayad, Mohamed F. ;
Fahmy, Nadia Z. ;
Rosenstiel, Stephen F. .
JOURNAL OF PROSTHETIC DENTISTRY, 2008, 99 (02) :123-130
[5]   EFFECT OF CROSS-LINKING AGENT CONTENT, MONOMER FUNCTIONALITY, AND REPEAT UNIT CHEMISTRY ON PROPERTIES OF UNFILLED RESINS [J].
BEATTY, MW ;
SWARTZ, ML ;
MOORE, BK ;
PHILLIPS, RW ;
ROBERTS, TA .
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 1993, 27 (03) :403-413
[6]   Effect of etching and airborne particle abrasion on the microstructure of different dental ceramics [J].
Borges, GA ;
Sophr, AM ;
de Goes, MF ;
Sobrinho, LC ;
Chan, DCN .
JOURNAL OF PROSTHETIC DENTISTRY, 2003, 89 (05) :479-488
[7]   Fracture Loads of All-Ceramic Crowns under Wet and Dry Fatigue Conditions [J].
Borges, Gilberto A. ;
Caldas, Danilo ;
Taskonak, Burak ;
Yan, Jiahau ;
Sobrinho, Lourenco Correr ;
de Oliveira, Wildomar Jose .
JOURNAL OF PROSTHODONTICS-IMPLANT ESTHETIC AND RECONSTRUCTIVE DENTISTRY, 2009, 18 (08) :649-655
[8]  
BRECKER SC, 1956, J PROS DENT, V6, P801
[9]  
Callister Jr WD, 2007, MAT SCI ENG INTRO, P207
[10]   Effect of different etching periods on the bond strength of a composite resin to a machinable porcelain [J].
Chen, JH ;
Matsumura, H ;
Atsuta, M .
JOURNAL OF DENTISTRY, 1998, 26 (01) :53-58