Localized corrosion susceptibility of Alloy 22 in chloride solutions: Part 2 - Effect of fabrication processes

被引：32

作者：

Dunn, DS ^{[1
]}

Pan, YM ^{[1
]}

Yang, L ^{[1
]}

Cragnolino, GA ^{[1
]}

机构：

[1] SW Res Inst, Ctr Nucl Waster Regulatory Analyses, San Antonio, TX 78238 USA

来源：

CORROSION | 2006年 / 62卷 / 01期

关键词：

alloy; 22; crevice corrosion; high-level radioactive waste; repassivation potential; welding;

D O I：

10.5006/1.3278250

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of fabrication processes on the localized corrosion susceptibility of Alloy 22 ([UNS N06022] 56Ni-22Cr-13.5Mo-3W-4Fe). a candidate container material for the disposal of high-level nuclear waste in the proposed repository at Yucca Mountain. Nevada. was assessed in chloride-containing solutions at temperatures ranging from 60 degrees C to 95 degrees C. The results of tests covering a range of metallurgical conditions, including as-welded. welded plus solution-annealed, and thermally aged materials. were compared with those for the as-received mill-annealed alloy. The localized corrosion susceptibility of Alloy 22 was determined by comparing the crevice corrosion repassivation potentials with corrosion potentials measured in separate tests. The crevice corrosion susceptibility was found to be dependent on temperature, chloride concentration, and the nitrate-to-chloride molar concentration ratio. Welding and short-term thermal aging decreased the localized corrosion resistance of Alloy 22 compared with the mill-annealed material.

引用

页码：3 / 12

页数：10

共 26 条

[1]

*ASTM, 2001, ANN BOOK STAND

[2]

*BECHT SAIC COMP L, 2001, TDREBSND000003 BECHT

[3]

*BECHT SAIC COMP L, 2000, SDDUDCSE000001 LLC B

[4]

*BECHT SAIC COMP L, 2004, ANLEBSMD000003

[5] THE WELDING METALLURGY OF HASTELLOY ALLOY-C-4, ALLOY-C-22, AND ALLOY-C-276 [J].

CIESLAK, MJ ;

HEADLEY, TJ ;

ROMIG, AD .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (11) :2035-2047

[6] THE USE OF NEW PHACOMP IN UNDERSTANDING THE SOLIDIFICATION MICROSTRUCTURE OF NICKEL-BASE ALLOY WELD METAL [J].

CIESLAK, MJ ;

KNOROVSKY, GA ;

HEADLEY, TJ ;

ROMIG, AD .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (12) :2107-2115

[7]

Cragnolino GA, 2002, MATER RES SOC SYMP P, V713, P53

[8]

CRAGNOLINO GA, 2001, P SCI BAS NUCL WA 24, V663, P507

[9]

*CRWMS M O, 2000, TDREBSMD000010 CRWMS

[10] An electrochemical approach to predicting long-term localized corrosion of corrosion-resistant high-level waste container materials [J].

Dunn, DS ;

Cragnolino, GA ;

Sridhar, N .

CORROSION, 2000, 56 (01) :90-104

← 1 2 3 →