MICROSTRUCTURE CHARACTERISTICS OF Ni3Al BASED INTERMETALLIC COMPOUNDS

被引：0
|
作者：
Malcharczikova, Jitka [1 ]
Pohludka, Martin [1 ]
Kursa, Miroslav [1 ]
机构：
[1] VSB Tech Univ Ostrava, Ostrava 70833, Czech Republic
来源：
CHEMICKE LISTY | 2012年 / 106卷
关键词：
micro-hardness; micro-structure; Ni3Al based alloy; SINGLE-CRYSTAL SUPERALLOYS;
D O I：
暂无
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
J. Malcharczikova, M. Pohludka, and M. Kursa (VSB-Technical University of Ostrava): Microstructure Characteristics of Ni3Al Based Intermetallic Compounds Observations were made in orientated state of non-alloyed intermetallic Ni3Al based compound (22-25 at.% of Al). The samples were solidified by Bridgman's technique. It was established that Ni22Al samples contained formations of Ni3Al (gamma') and solid solution of nickel (gamma), Ni25Al samples contained Ni3Al only. The differences of mechanical properties were not manifested at measurement of micro-hardness, which is for all the samples approximately within the interval from 240 to 260 HV 0.05.
引用
收藏
页码：S474 / S475
页数：2
相关论文
共 50 条
  • [1] High temperature intermetallic compounds Ni3Al
    Kursa, M
    Hyspecka, L
    Drapala, J
    Karnik, T
    Losertova, M
    JOURNAL DE PHYSIQUE IV, 1995, 5 (C7): : 123 - 128
  • [2] High temperature intermetallic compounds Ni3Al
    Kursa, M.
    Hypeska, L.
    Drapala, J.
    Karnik, T.
    Losertova, M.
    Journal De Physique, 1995, 5 (07): : 7 - 123
  • [3] Evolution of texture and microstructure during processing of Ni3Al based intermetallic alloys
    Ray, RK
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2002, 55 (06): : 501 - 518
  • [4] Deformation microstructure of Ni3Al intermetallic compound macroalloyed with Pd
    Sun, J
    Lee, CS
    Lai, JKL
    MATERIALS LETTERS, 1997, 31 (1-2) : 1 - 4
  • [5] Microstructure and mechanical properties of transient liquid phase (TLP)-bonded Ni3Al intermetallic compounds
    Samani, M. Soltani
    Bahrami, A.
    Karimzadeh, F.
    MATERIALS TODAY COMMUNICATIONS, 2019, 21
  • [6] Ordering kinetics and atomic mobility in Ni3Al intermetallic compounds
    Dimitrov, C
    Dimitrov, O
    DEFECT AND DIFFUSION FORUM/JOURNAL, 1997, 143 : 251 - 256
  • [7] Oxidation of gamma'-Ni3Al and gamma'-Ni3Al(Si) intermetallic compounds at low-oxygen pressures
    Yi, HC
    Smeltzer, WW
    Petric, A
    OXIDATION OF METALS, 1996, 45 (3-4): : 281 - 299
  • [8] On the strength of Ni3Al based compounds
    Kruml, T
    Martin, JL
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 1861 - 1866
  • [9] Microjoining of Ni3Al based intermetallic thin foils
    Jozwik, P.
    Bojar, Z.
    Kolodziejczak, P.
    MATERIALS SCIENCE AND TECHNOLOGY, 2010, 26 (04) : 473 - 477
  • [10] Yielding description for a Ni3Al based intermetallic alloy
    Chen, Lei
    Wen, Weidong
    Cui, Haitao
    MATERIALS & DESIGN, 2012, 41 : 192 - 197
12345