The effects of Co-Ti co-doping on the magnetic, electrical, and magnetodielectric behaviors of M-type barium hexaferrites

Magnetic, electrical and magnetodielectric properties have been studied in Co-Ti co-doped M-type hexaferrite BaCoxTixFe12-2xO19 (x = 0 similar to 4). With the incorporation of Co-Ti, both their ferromagnetic magnetization and coercivity have been greatly changed. The temperature dependent magnetization curve shows a apparent hump at around 420 K, likely in association with more complicated cycloidal spin ordering, which is closely related to ferroelectric polarization. Interestingly, a significantly enhancement in resistivity (similar to 3 orders in magnitude) can be obtained in co-doped samples (x > 2), which is beneficial for magnetoelectric properties. The magnetoelectric effect were examined by dielectric tunibility under external magnetic field, which shows apparent tunability up to similar to-3% for sample with x = 2 at 1T magnetic field, further supporting it is a room temperature single phase mutliferroic material. (C) 2013 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution 3.0 Unported License.