The electrochemical behaviors of methylene blue on the surface of nanostructured NiWO4 prepared by coprecipitation method

A simple coprecipitation method was used for preparation of monoclinic nanostructured NiWO4 from an aqueous solution at a fixed pH and temperature of 7.0 and 80 A degrees C, respectively. The prepared material was characterized by X-ray diffraction, scanning electron microscopy, photoluminescence spectroscopy, and electrochemical measurements. Nano-NiWO4 was incorporated into a carbon paste electrode and by means of cyclic voltammetry; the electrochemical behavior of methylene blue on the surface of nano-NiWO4 was investigated. A mechanism on terms of obtained cyclic voltammograms showing one reduction peak and two sequential oxidation peaks was suggested by emphasizing on the stabilizing role of nano-NiWO4 for semi-methylene blue. A diffusion coefficient of 5.30 x 10(-6) cm(2)/s was gained for methylene blue.