Study on Rheological Properties of Bituminous Binders and Mixtures Containing Waste Printed Circuit Boards (PCBs) and SBR Compound Modified Bitumen

被引：6

作者：

Meng, Yongjun ^{[1
,2
,3
]}

Liao, Yongjie ^{[1
]}

Liu, Zhirong ^{[1
]}

Chen, Jing ^{[1
]}

Yang, Xiaolong ^{[1
]}

Rong, Hongliu ^{[1
]}

机构：

[1] Guangxi Univ, Coll Civil Engn & Architecture, Nanning 530004, Peoples R China

[2] Minist Educ, Key Lab Disaster Prevent & Engn Safety, Nanning 530004, Peoples R China

[3] Natl High Performance Comp Ctr Nanning Branch, Nanning 530004, Peoples R China

来源：

MATERIALS | 2021年 / 14卷 / 07期

基金：

中国国家自然科学基金;

关键词：

modified bitumen; printed circuit boards (PCBs); SBR; high temperature properties; bituminous mixture properties;

D O I：

10.3390/ma14071697

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Improper handling of waste printed circuit boards (PCBs) can cause serious pollution to the water and soil environments. In order to explore a new method of recycling waste PCBs, this study investigated the effect of PCBs and butadiene styrene rubber (SBR) on the rheological properties of neat bitumen. The dynamic shear rheological (DSR) test was used to study the effect of different PCB contents on the high-temperature rheological properties of SBR-modified bitumen. Fluorescence microscopy and Fourier-transform infrared spectroscopy were used to study the microstructure change law and modification mechanism of PCB and SBR composite modified bitumen. Finally, the feasibility of the bitumen properties was verified through a test of the bituminous mixture properties. The DSR test results showed that the addition of PCBs improves the elastic recovery modulus, dynamic shear modulus, and rutting factor of SBR-modified bitumen, indicating that the high-temperature properties were improved. Infrared spectroscopy analysis revealed that a new absorption peak was generated in the infrared spectrum of the compound bitumen after the addition of PCBs, and the intensity of the original absorption peak also changed, indicating that PCBs and SBR-modified bitumen were mainly physically blended and accompanied by a weak chemical reaction. It was further found that the absorption peak of the unsaturated C=C double bond was significantly enhanced, and the increase in the content of the unsaturated bond C=C in the main chain of the polymer significantly increases the stiffness of the bitumen. Macroscopically, the high-temperature rutting resistance was improved to a certain extent. The fluorescence diagram shows that when PCBs do not exceed 10%, the PCBs can form a homogeneous structure and be dispersed in SBR-modified bitumen. The road test of PCBs and SBR composite modified bituminous mixtures showed that PCBs can significantly improve the rutting resistance and water stability of SBR-modified bitumen at high temperatures at the recommended optimum content. The crack resistance at low temperatures is weakened but still meets actual engineering requirements. The correlation analysis between the properties of bitumen and bituminous mixtures is carried out based on grey correlation theory. The results show that the index of modified bitumen has a very good guiding effect on the bituminous mixture properties. The development of PCBs and SBR composite-modified bitumen provides a new practical method for recycling waste PCBs.