Effect of Al alloys on selective laser melting behaviour and microstructure of in situ formed particle reinforced composites

被引:127
作者
Dadbakhsh, S. [1 ]
Hao, L. [1 ]
机构
[1] Univ Exeter, Coll Engn Math & Phys Sci, Exeter, Devon, England
关键词
Aluminium alloys; Metal matrix composites; Laser processing; Powder metallurgy; Microstructure; MG; MECHANISMS; QUALITY; SLM;
D O I
10.1016/j.jallcom.2012.06.097
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
This work investigates the effects of various Al alloys (including Al, AlMg1SiCu, and AlSi10Mg), mixed with 15 wt% Fe2O3, on the selective laser melting (SLM) facilitated in situ reaction and formation of Al metal matrix composite (MMC) components. The results contribute to the development of medium/high strength Al composite parts which can be produced as complex net-shape products via the SLM process. Visual observation and computed tomography (CT) scanning reveal the best SLM consolidation performance and the lowest porosity for AlSi10Mg. SLM facilitated in situ reaction and subsequent rapid solidification introduce very fine particles (down to similar to 50-100 nm), reinforcing the microstructure of all Al (alloy) composites. The particles are Al-Fe intermetallics, Al oxides such as alpha-Al2O3, plus Si crystals (alone or in combination) depending on the alloy composition. Ultrafine/nanoscale dendritic feature appears in the reinforced matrix of AlSi10Mg/15 wt% Fe2O3, in contrast with featureless matrix of Al/15 wt% Fe2O3. The in situ particle reinforced Al (alloy) composites are significantly harder than corresponding conventionally manufactured (e. g. casting) Al alloys without Fe2O3, due to superior microstructural characteristics such as featureless or very fine dendritic matrix, ultrafine/nanoscale particles, and also enhanced solid solubility of the SLM products. (C) 2012 Elsevier B. V. All rights reserved.
引用
收藏
页码:328 / 334
页数:7
相关论文
共 27 条
[1]   The microstructure and mechanical strength of Al-6061-T6 GMA welds obtained with the modified indirect electric arc joint [J].
Ambriz, R. R. ;
Barrera, G. ;
Garcia, R. ;
Lopez, V. H. .
MATERIALS & DESIGN, 2010, 31 (06) :2978-2986
[2]  
Ashby MF, 2005, LASER PROCESSING OF ENGINEERING MATERIALS: PRINCIPLES, PROCEDURE AND INDUSTRIAL APPLICATION, P261
[3]  
ASM Handbook, 1992, ASM HDB, V02
[4]   Additive manufactured AlSi10Mg samples using Selective Laser Melting (SLM): Microstructure, high cycle fatigue, and fracture behavior [J].
Brandl, Erhard ;
Heckenberger, Ulrike ;
Holzinger, Vitus ;
Buchbinder, Damien .
MATERIALS & DESIGN, 2012, 34 :159-169
[5]   High Power Selective Laser Melting (HP SLM) of Aluminum Parts [J].
Buchbinder, D. ;
Schleifenbaum, H. ;
Heidrich, S. ;
Meiners, W. ;
Bueltmann, J. .
LASERS IN MANUFACTURING 2011: PROCEEDINGS OF THE SIXTH INTERNATIONAL WLT CONFERENCE ON LASERS IN MANUFACTURING, VOL 12, PT A, 2011, 12 :271-278
[6]   Effect of selective laser melting layout on the quality of stainless steel parts [J].
Dadbakhsh, S. ;
Hao, L. ;
Sewell, N. .
RAPID PROTOTYPING JOURNAL, 2012, 18 (03) :241-249
[7]  
Dadbakhsh S., 2009, INNOVATIVE DEV DESIG, P319
[8]   In Situ Formation of Particle Reinforced Al Matrix Composite by Selective Laser Melting of Al/Fe2O3 Powder Mixture [J].
Dadbakhsh, Sasan ;
Hao, Liang .
ADVANCED ENGINEERING MATERIALS, 2012, 14 (1-2) :45-48
[9]   Kinetics of thermite reaction in Al-Fe2O3 system [J].
Fan, RH ;
Lü, HL ;
Sun, KN ;
Wang, WX ;
Yi, XB .
THERMOCHIMICA ACTA, 2006, 440 (02) :129-131
[10]   Equilibrium and non-equilibrium intermetallic phases in Al-Fe and Al-Fe-Si alloys [J].
Griger, A ;
Stefaniay, V .
JOURNAL OF MATERIALS SCIENCE, 1996, 31 (24) :6645-6652