Effect of ageing on microstructure and mechanical properties of a multi-directionally forged Mg-6Al-1Zn alloy

被引：32

作者：

Miura, H. ^{[1
]}

Maruoka, T. ^{[1
]}

Jonas, J. J. ^{[2
]}

机构：

[1] Univ Electrocommun, Dept Mech Engn & Intelligent Syst, UEC Tokyo, Chofu, Tokyo 1828585, Japan

[2] McGill Univ, Dept Mat Engn, Montreal, PQ H3A 2B2, Canada

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 563卷

关键词：

Mg alloy; Multi-directional forging; Ultrafine-grained materials; Twinning; Ageing; Mechanical properties; MAGNESIUM ALLOY; DEFORMATION; AZ31;

D O I：

10.1016/j.msea.2012.11.021

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Samples of an AZ61Mg alloy were multi-directionally forged (MDFed) at room temperature employing small pass strains of Delta epsilon=0.1 to maximum cumulative strains of Sigma Delta epsilon =2.5. Ageing at 403 K for 1 h was carried out before and during MDFing. The coarse initial grains were gradually subdivided into ultrafine ones by mechanical twinning. Twin formation effectively suppressed the development of sharp texture and in this way enabled severe plastic deformation to take place at ambient temperature. Simple ageing of the MDFed sample lowered the strength. However, a combined process of ageing and MDFing increased the hardness and yield stress while it slightly decreased ductility. Good mechanical properties of 500 MPa yield stress, 540 MPa ultimate tensile strength and 4% plastic strain to fracture were achieved. (c) 2012 Elsevier B.V. All rights reserved.

引用

页码：53 / 59

页数：7

共 14 条

[1] Influence of grain size on the compressive deformation of wrought Mg-3Al-1Zn [J].

Barnett, MR ;

Keshavarz, Z ;

Beer, AG ;

Atwell, D .

ACTA MATERIALIA, 2004, 52 (17) :5093-5103

[2] Microstructures and mechanical properties of AZ61 magnesium alloy after processing with high presser torsion [J].

Harai, Yosuke ;

Kai, Masaaki ;

Kaneko, Kenji ;

Horita, Zenji .

JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2007, 71 (02) :213-217

[3] Rapidly solidified powder metallurgy Mg97Zn1Y2Alloys with excellent tensile yield strength above 600 MPa [J].

Kawamura, Y ;

Hayashi, K ;

Inoue, A ;

Masumoto, T .

MATERIALS TRANSACTIONS, 2001, 42 (07) :1172-1176

[4] Formation and mechanical properties of Mg97Zn1RE2 alloys with long-period stacking ordered structure [J].

Kawamura, Yoshihito ;

Yamasaki, Michiaki .

MATERIALS TRANSACTIONS, 2007, 48 (11) :2986-2992

[5] Roles of deformation twinning and dislocation slip in the fatigue failure mechanism of AZ31 Mg alloys [J].

Koike, J. ;

Fujiyama, N. ;

Ando, D. ;

Sutou, Y. .

SCRIPTA MATERIALIA, 2010, 63 (07) :747-750

[6] Variant selection during secondary twinning in Mg-3%Al [J].

Martin, E. ;

Capolungo, L. ;

Jiang, L. ;

Jonas, J. J. .

ACTA MATERIALIA, 2010, 58 (11) :3970-3983

[7] Microstructure and mechanical properties of multi-directionally forged Mg-Al-Zn alloy [J].

Miura, H. ;

Maruoka, T. ;

Yang, X. ;

Jonas, J. J. .

SCRIPTA MATERIALIA, 2012, 66 (01) :49-51

[8] Multi-directional forging of AZ61Mg alloy under decreasing temperature conditions and improvement of its mechanical properties [J].

Miura, H. ;

Yu, G. ;

Yang, X. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (22-23) :6981-6992

[9] Variant selection of primary, secondary and tertiary twins in a deformed Mg alloy [J].

Mu, Sijia ;

Jonas, John J. ;

Gottstein, Guenter .

ACTA MATERIALIA, 2012, 60 (05) :2043-2053

[10] [112BAR2](11BAR23) SLIP SYSTEM IN MAGNESIUM [J].

OBARA, T ;

YOSHINGA, H ;

MOROZUMI, S .

ACTA METALLURGICA, 1973, 21 (07) :845-853

← 1 2 →