Polyurethane membrane prepared via a dry/wet phase inversion method for protein adsorption

被引:0
作者
Huang, SL [1 ]
Ou, CF
Lai, JY
机构
[1] Natl Chin Yi Inst Technol, Dept Chem Engn, Taichung 41111, Taiwan
[2] Chung Yuan Christian Univ, Dept Chem Engn, Chungli 32023, Taiwan
关键词
protein adsorption; polyurethane; dry/wet; phase inversion;
D O I
10.1002/(SICI)1097-4628(19991107)74:63.0.CO;2-%23
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Hydroxyl-terminated polybutadiene (HTPB)- and 4,4'-dicyclohexyl-methane (H12MDI)-based polyurethanes (PUs) were synthesized by solution polymerization. PU membranes were prepared by a dry/wet phase inversion method. Protein adsorption ratio of fibrinogen to albumin (F/A molar ratio) was measured. Low F/A molar ratio was found on these PUs. It was found that surface composition of these PUs has a subtle effect on F/A adsorption molar ratio. The F/A molar ratio was increased as the increase of hard segment content distributed on the surface. The variation of surface composition of these membranes and the effect on the F/A molar ratio were investigated by the difference in surface energy between nonpolar HTPB soft segment and polar hard segment, concentration, and temperature of coagulation medium, polymer content, and alcohol type. The C=O/C=C ratio, frequency shift, and difference (Delta nu) as a measure of polymer homogeneity and the average strength of interpolymer hydrogen bonds were utilized to study the surface composition. (C) 1999 John Wiley & Sons, Inc.
引用
收藏
页码:1334 / 1340
页数:7
相关论文
共 25 条
[1]   PROTEIN ADSORPTION TO POLYMER PARTICLES - ROLE OF SURFACE-PROPERTIES [J].
ABSOLOM, DR ;
ZINGG, W ;
NEUMANN, AW .
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 1987, 21 (02) :161-171
[2]  
BRASH JL, 1979, J POLYM SCI POL SYM, P377
[3]  
CHUANG HYK, 1984, J BIOMED MATER RES, V18, P547, DOI 10.1002/jbm.820180508
[4]   HYDROGEN-BONDING IN POLYMER BLENDS .1. FTIR STUDIES OF URETHANE ETHER BLENDS [J].
COLEMAN, MM ;
SKROVANEK, DJ ;
HU, JB ;
PAINTER, PC .
MACROMOLECULES, 1988, 21 (01) :59-65
[5]  
COSTA VS, 1980, J COLLOID INTERF SCI, V76, P594
[6]  
DON TM, 1992, J APPL POLYM SCI, V43, P2193
[7]   EFFECTS OF ALKYL GRAFTING ON SURFACE-PROPERTIES AND BLOOD COMPATIBILITY OF POLYURETHANE BLOCK COPOLYMERS [J].
GRASEL, TG ;
PIERCE, JA ;
COOPER, SL .
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 1987, 21 (07) :815-842
[8]  
HOFFMAN AS, 1982, ACS ADV CHEM SER, V3, P199
[9]   ON THE GAS-PERMEABILITY OF HYDROXYL TERMINATED POLYBUTADIENE BASED POLYURETHANE MEMBRANES [J].
HUANG, SL ;
LAI, JY .
JOURNAL OF MEMBRANE SCIENCE, 1995, 105 (1-2) :137-145
[10]   Structure effect on the peel strength of polyurethane [J].
Huang, SL ;
Yu, SJ ;
Lai, JY .
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 1998, 12 (04) :445-456