Predicting Oxidation-Limited Lifetime of Thin-Walled Components of NiCrW Alloy 230

被引:41
作者
Duan, R. [1 ]
Jalowicka, A. [1 ]
Unocic, K. [2 ]
Pint, B. A. [2 ]
Huczkowski, P. [1 ]
Chyrkin, A. [1 ]
Gruener, D. [1 ]
Pillai, R. [1 ]
Quadakkers, W. J. [1 ]
机构
[1] Forschungszentrum Julich, Inst Energy & Climate Res, IEK-2, D-52425 Julich, Germany
[2] Oak Ridge Natl Lab, Div Mat Sci & Technol, Oak Ridge, TN 37831 USA
来源
OXIDATION OF METALS | 2017年 / 87卷 / 1-2期
关键词
ALLOY; 230; Chromia scales; Lifetime; Subscale depletion; Wall thickness loss; HIGH-TEMPERATURE OXIDATION; NI-BASE ALLOYS; CYCLIC-OXIDATION; SPECIMEN THICKNESS; BREAKAWAY OXIDATION; DEPLETION PROFILES; INTERNAL OXIDATION; CREEP-PROPERTIES; SCALE FORMATION; CHROMIA SCALES;
D O I
10.1007/s11085-016-9653-9
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Using alloy 230 as an example, a generalized oxidation lifetime model for chromia-forming Ni-base wrought alloys is proposed, which captures the most important damaging oxidation effects relevant for component design: wall thickness loss, scale spallation, and the occurrence of breakaway oxidation. For deriving input parameters and for verification of the model approach, alloy 230 specimens with different thicknesses were exposed for different times at temperatures in the range 950-1050 A degrees C in static air. The studies focused on thin specimens (0.2-0.5 mm) to obtain data for critical subscale depletion processes resulting in breakaway oxidation within reasonably achievable test times up to 3000 h. The oxidation kinetics and oxidation-induced subscale microstructural changes were determined by combining gravimetric data with results from scanning electron microscopy with energy dispersive X-ray spectroscopy. The modeling of the scale spallation and re-formation was based on the NASA cyclic oxidation spallation program, while a new model was developed to describe accelerated oxidation occurring after longer exposure times in the thinnest specimens. The calculated oxidation data were combined with the reservoir model equation, by means of which the relation between the consumption and the remaining concentration of Cr in the alloy was established as a function of temperature and specimen thickness. Based on this approach, a generalized lifetime diagram is proposed, in which wall thickness loss is plotted as a function of time, initial specimen thickness, and temperature. The time to reach a critical Cr level at the scale/alloy interface of 10 wt% is also indicated in the diagrams.
引用
收藏
页码:11 / 38
页数:28
相关论文
共 66 条
[51]  
Schutze M., 1997, SERIES ON CORROSION
[52]  
Sims C. T., 1987, SUPPERALLOYS II HIGH
[53]   A deterministic interfacial cyclic oxidation spalling model [J].
Smialek, JL .
ACTA MATERIALIA, 2003, 51 (02) :469-483
[54]   High-temperature oxidation behavior of a wrought Ni-Cr-W-Mn-Si-La alloy [J].
Tawancy, HM .
OXIDATION OF METALS, 1996, 45 (3-4) :323-348
[55]   HIGH-TEMPERATURE CREEP-BEHAVIOR OF AN NI-CR-W-B ALLOY [J].
TAWANCY, HM .
JOURNAL OF MATERIALS SCIENCE, 1992, 27 (23) :6481-6489
[56]   Competition between stress generation and relaxation during oxidation of an Fe-Cr-Al-Y alloy [J].
Tolpygo, VK ;
Clarke, DR .
OXIDATION OF METALS, 1998, 49 (1-2) :187-212
[57]   Growth mechanism of Cr2O3 scales: Oxygen and chromium diffusion, oxidation kinetics and effect of yttrium [J].
Tsai, SC ;
Huntz, AM ;
Dolin, C .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 212 (01) :6-13
[58]  
WAGNER C, 1959, Z ELEKTROCHEM, V63, P772
[59]   COMPOSITIONAL CHANGES IN UNDERLYING ALLOY DURING PROTECTIVE OXIDATION OF ALLOYS [J].
WHITTLE, DP ;
EVANS, DJ ;
SCULLY, DB ;
WOOD, GC .
ACTA METALLURGICA, 1967, 15 (09) :1421-&
[60]   OXIDATION OF FINITE SAMPLES OF HEAT-RESISTANT ALLOYS [J].
WHITTLE, DP .
CORROSION SCIENCE, 1972, 12 (11) :869-&