Residual stress effects on fatigue crack growth in a Ti-6Al-4V friction stir weld

被引：60
|
作者：
Pasta, S. [1 ]
Reynolds, A. P. [2 ]
机构：
[1] Univ Palermo, Dipartimento Meccan, I-90128 Palermo, Italy
[2] Univ S Carolina, Dept Mech Engn, Columbia, SC 29208 USA
来源：
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2008年 / 31卷 / 07期
关键词：
fatigue crack growth propagation; friction stir welding; residual stress; titanium alloy;
D O I：
10.1111/j.1460-2695.2008.01258.x
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Recent studies have illustrated a predominant role of the residual stress on the fatigue crack growth in friction stir welded joints. In this study, the role of the residual stress on the propagation of fatigue cracks orthogonal to the weld direction in a friction stir welded Ti-6Al-4V joint was investigated. A numerical prediction of the fatigue crack growth rate in the presence of the residual stresses was carried out using AFGROW software; reasonable correspondence between the predictions and the experimental results were observed when the effects of residual stress were included in the simulation.
引用
收藏
页码：569 / 580
页数：12
相关论文
共 50 条
  • [21] Effects of Shot-Peening on Fretting Fatigue Crack Growth Behavior in Ti-6Al-4V
    Mall, S.
    Jain, V. K.
    Fadag, H. A.
    STRAIN, 2011, 47 : E305 - E318
  • [22] The stir zone microstructure and its formation mechanism in Ti-6Al-4V friction stir welds
    Zhou, L.
    Liu, H. J.
    Liu, P.
    Liu, Q. W.
    SCRIPTA MATERIALIA, 2009, 61 (06) : 596 - 599
  • [23] Crystallography of Fatigue Crack Initiation and Growth in Fully Lamellar Ti-6Al-4V
    Pilchak, A. L.
    Williams, R. E. A.
    Williams, J. C.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (01): : 106 - 124
  • [24] Microstructural evolution mechanism of hydrogenated Ti-6Al-4V in the friction stir welding and post-weld dehydrogenation process
    Liu, H. J.
    Zhou, L.
    Liu, Q. W.
    SCRIPTA MATERIALIA, 2009, 61 (11) : 1008 - 1011
  • [25] Heat Treatment to Improve Fatigue Strength of Friction Stir Welded Ti-6Al-4V Alloy Butt Joint
    Nakai, Masaaki
    Niinomi, Mitsuo
    Ishida, Yu
    Liu, Huihong
    Fujii, Hidetoshi
    Ninomiya, Takashi
    MATERIALS TRANSACTIONS, 2017, 58 (08) : 1223 - 1226
  • [26] Effects of microstructure on fretting fatigue crack initiation behavior of Ti-6Al-4V
    Mall, S
    Namjoshi, SA
    Porter, W
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 383 (02): : 334 - 340
  • [27] Residual stress and microstructure effects on fatigue crack growth in AA2050 friction stir welds
    Pouget, G.
    Reynolds, A. P.
    INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (03) : 463 - 472
  • [28] Fretting fatigue crack initiation behavior of Ti-6Al-4V
    Mall, S
    Jain, VK
    Oshi, SAN
    Lykins, CD
    FRETTING FATIGUE: ADVANCES IN BASIC UNDERSTANDING AND APPLICATIONS, 2003, 1425 : 338 - 352
  • [29] The Effect of Friction Stir Welding on Corrosion Behavior of Ti-6Al-4V
    Nasresfahani, Ali Reza
    Soltanipur, Abdol Reza
    Farmanesh, Khosro
    Ghasemi, Ali
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (09) : 4311 - 4318
  • [30] Peak temperatures during friction stir welding of Ti-6Al-4V
    Edwards, P.
    Ramulu, M.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2010, 15 (06) : 468 - 472
12345