Effects of RE and vanadium on microalloyed steel

被引:0
作者
Lin, Q
Wang, HB
Lu, XL
Song, B
Tang, L
Jia, LD
机构
[1] Univ Sci & Technol Beijing, Dept Phys Chem, Beijing 100083, Peoples R China
[2] Panzhihua Iron & Steel Grp Co, Panzhihua 617000, Peoples R China
[3] Chinese Soc Rare Earths, Beijing 100081, Peoples R China
关键词
rare earths; vanadium; precipitation; recrystallization; microalloying;
D O I
暂无
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
The effects of RE were studied by TEM, SEM, ICP and thermal simulation methods in vanadium microalloyed steel. The content of RE in the solid solution can reach the order of 10(-5) similar to 10(-4) in steel. The solid solution of RE was found to reduce the stability of precipitated V (C, N), impede the precipitation of V (C, N) in austenite, and accelerate and refine the precipitation of V(C, N) in ferrite. The combined effect of RE and V is to delay the dynamic recrystallization, refine the grains and second phase particles, and to promote the precipitation of V(C,N) obviously. Thus the microalloying with RE and V leads to raising the strength and toughness of steel.
引用
收藏
页码:36 / 40
页数:5
相关论文
共 7 条
[1]   EFFECT OF VANADIUM AND MOLYBDENUM ADDITION ON HIGH-TEMPERATURE RECOVERY, RECRYSTALLIZATION AND PRECIPITATION BEHAVIOR OF NIOBIUM-BASED MICROALLOYED STEELS [J].
AKBEN, MG ;
BACROIX, B ;
JONAS, JJ .
ACTA METALLURGICA, 1983, 31 (01) :161-174
[2]  
DU T, 1991, P 2 INT C RE DEV APP, P906
[3]  
Lin Q., 1990, CHIN J MET SCI TECHN, V6, P415
[4]  
LIN Q, 1997, J UNIV SCI TECHNOL B, V4, P34
[5]  
Lin Q., 1997, J CHIN RARE EARTH SO, V22, P228
[6]  
WANG HB, 1996, STUDY EFFECT RE VANA, P67
[7]  
Ye W, 1997, J RARE EARTH, V15, P201