PROCESSING AND PROPERTIES OF Al0.3CrCuFeNi2 SINGLE CRYSTAL HIGH-ENTROPY ALLOY

被引:2
|
作者
Zhang Sufang [1 ]
Yang Xiao [1 ]
Zhang Yong [1 ]
机构
[1] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China
基金
中国国家自然科学基金;
关键词
Al0.3CrCuFeNi2 high-entropy alloy; EBSD; orientation analysis; mechanical property; MICROSTRUCTURE EVOLUTION; MECHANICAL-PROPERTIES; TENSILE PROPERTIES; SUPERALLOY;
D O I
10.3724/SP.J.1037.2013.00540
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The high-entropy alloy is a class of new metal material, its dominant element is generally more than three, and its mixing entropy is high and easy to form a solid solution structure. A large number of investigations show that high-entropy alloy possess excellent high temperature phase stability and softening resistance, which is superior to traditional superalloy. The Al0.3CrCuFeNi2 high-entropy alloy is studied by using once Bridgman solidification at different draw rates (10, 30 and 150 mu m/s) and twice Bridgman solidification at 10 mu m/s draw rate, the corresponding microstructure are analyzed. The EBSD technique is applied to detect the alloy growth orientation and grain boundary misorientation angle of alloys by once and twice Bridgman solidification at 10 mu m/s draw rate. The room temperature tensile mechanical properties of Al0.3CrCuFeNi2 high-entropy alloy by twice Bridgman solidification at 10 mu m/s draw rate and suction casting are studied. The results show that the primary spacing of dendritic of Al0.3CrCuFeNi2 high-entropy alloy by Bridgman solidification at 10 mu m/s draw rate is larger than other draw rates and suction casting, while the growth orientation angle of dendrite dry is smaller than others. The orientation is close to the < 001 > direction after twice Bridgman solidification at 10 mu m/s draw rate, and most of grain boundary misorientation angle are less than 5 degrees. Compared with suction casting samples, yield strength, tensile strength and elongation of Al0.3CrCuFeNi2 high-entropy alloy by using twice Bridgman solidification increased by 34.6%, 10.2% and 40%.
引用
收藏
页码:1473 / 1480
页数:8
相关论文
共 27 条
  • [11] EFFECT OF MISORIENTATION ON THE TENSILE PROPERTIES OF SRR99 SUPERALLOY BICRYSTALS
    Li Xiaoyang
    Li Peng
    Zhou Yizhou
    Jin Tao
    Zhang Zhefeng
    [J]. ACTA METALLURGICA SINICA, 2013, 49 (03) : 351 - 357
  • [12] Evolution of microstructure, hardness, and corrosion properties of high-entropy Al0.5CoCrFeNi alloy
    Lin, Chun-Ming
    Tsai, Hsien-Lung
    [J]. INTERMETALLICS, 2011, 19 (03) : 288 - 294
  • [13] Liu J, 2005, J HUNAN I ENG, V15, P49
  • [14] A Successful Synthesis of the CoCrFeNiAl0.3 Single-Crystal, High-Entropy Alloy by Bridgman Solidification
    Ma, S. G.
    Zhang, S. F.
    Gao, M. C.
    Liaw, P. K.
    Zhang, Y.
    [J]. JOM, 2013, 65 (12) : 1751 - 1758
  • [15] Mechanical properties of Nb25Mo25Ta25W25 and V20Nb20Mo20Ta20W20 refractory high entropy alloys
    Senkov, O. N.
    Wilks, G. B.
    Scott, J. M.
    Miracle, D. B.
    [J]. INTERMETALLICS, 2011, 19 (05) : 698 - 706
  • [16] Decomposition in multi-component AlCoCrCuFeNi high-entropy alloy
    Singh, S.
    Wanderka, N.
    Murty, B. S.
    Glatzel, U.
    Banhart, J.
    [J]. ACTA MATERIALIA, 2011, 59 (01) : 182 - 190
  • [17] Diffusion barrier properties of AlMoNbSiTaTiVZr high-entropy alloy layer between copper and silicon
    Tsai, Ming-Hung
    Yeh, Jien-Wei
    Gan, Jon-Yiew
    [J]. THIN SOLID FILMS, 2008, 516 (16) : 5527 - 5530
  • [18] On the elemental effect of AlCoCrCuFeNi high-entropy alloy system
    Tung, Chung-Chin
    Yeh, Jien-Wei
    Shun, Tao-tsung
    Chen, Swe-Kai
    Huang, Yuan-Sheng
    Chen, Hung-Cheng
    [J]. MATERIALS LETTERS, 2007, 61 (01) : 1 - 5
  • [19] A Multilevel Model for Elastic-Plastic Contact Between a Sphere and a Flat Rough Surface
    Wang, F. Steven
    Block, Joseph M.
    Chen, W. Wayne
    Martini, Ashlie
    Zhou, Kun
    Keer, Leon M.
    Wang, Q. Jane
    [J]. JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2009, 131 (02): : 1 - 6
  • [20] Prediction of high-entropy stabilized solid-solution in multi-component alloys
    Yang, X.
    Zhang, Y.
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2012, 132 (2-3) : 233 - 238