Preparation of Shrinkage Compensating Concrete with HCSA Expansive Agent

被引:0
|
作者
Li, Changcheng [1 ]
Jia, Fujia [1 ]
机构
[1] China Bldg Mat Acad, Guanzhuang Dongli 1, Beijing, Peoples R China
来源
3RD ANNUAL INTERNATIONAL WORKSHOP ON MATERIALS SCIENCE AND ENGINEERING (IWMSE2017) | 2017年 / 250卷
关键词
D O I
10.1088/1757-899X/250/1/012037
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Shrinkage compensating concrete (SCC) has become one of the best effective methods of preventing and reducing concrete cracking. SCC is prepared by HCSA high performance expansive agent for concrete which restrained expansion rate is optimized by 0.057%. Slump, compressive strength, restrained expansion rate and cracking resistance test were carried out on SCC. The results show that the initial slump of fresh SCC was about 220mm-230mm, while slump after 2 hours was 180mm-200mm. The restrained expansion rate of SCC increased with the mixing amount of expansive agent. After cured in water for 14 days, the restrained expansion rate of C35 and C40 SCC were 0.020%-0.032%. With the dosage of expansive agent increasing, restrained expansion rate of SCC increased, maximum compressive stress and cracking stress improved, cracking temperature fell, thus cracking resistance got effectively improvement.
引用
收藏
页数:6
相关论文
共 50 条
  • [11] Study on the Delayed Ettringite Formation in Massive Shrinkage Compensating Concrete with U-Type Expansive Agent
    Wang, Qian
    Ren, Zhengyue
    Zhang, Zhe
    ECOLOGICAL ENVIRONMENT AND TECHNOLOGY OF CONCRETE, 2011, 477 : 340 - +
  • [12] The influence of the hydration procedure of MgO expansive agent on the expansive behavior of shrinkage-compensating mortar
    Cao, Fengze
    Yan, Peiyu
    CONSTRUCTION AND BUILDING MATERIALS, 2019, 202 : 162 - 168
  • [13] Synergistic Effect of MgO-based Expansive Agent and Shrinkage Reducing Admixture on Compensating the Shrinkage of Cementitious Materials
    Zhang, Zhibin
    Xu, Lingling
    Tang, Mingshu
    ADVANCES IN STRUCTURES, PTS 1-5, 2011, 163-167 : 2350 - 2355
  • [14] Effect of Shrinkage Reducing Agent and HCSA Expansion Agent on Mechanical Properties and Shrinkage Properties of UHPC
    Gong J.
    Luo H.
    Zhang Y.
    Gong X.
    Xie Z.
    Wu W.
    Dai Y.
    Cailiao Daobao/Materials Reports, 2021, 35 (08): : 8042 - 8048and8063
  • [15] Autogenous shrinkage of shrinkage-compensating concrete
    Chen, Zhicheng
    Yan, Peiyu
    Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2010, 38 (04): : 568 - 573
  • [16] Compensation effect of expansive agent on shrinkage of self-compacting concrete
    Dong Rong-zhen
    Wei Jun
    Qi Yun-xuan
    Guo Liang-ting
    Chen Bing
    Liu You
    Wei Ran
    SUSTAINABLE DEVELOPMENT OF URBAN AND RURAL AREAS, 2014, 507 : 401 - 405
  • [17] Preparation and research of concrete shrinkage reducing agent
    Lin Yanmei
    OPTOELECTRONIC MATERIALS AND DEVICES (ICOMD 2020), 2021, 11767
  • [18] Experimental Study on Freezing and Thawing Cycles of Shrinkage-Compensating Concrete with Double Expansive Agents
    Guo, Jinjun
    Guo, Ting
    Zhang, Shiwei
    Lu, Yan
    MATERIALS, 2020, 13 (08)
  • [19] Shrinkage-compensating concrete floors
    King, Stephen M.
    Construction Specifier, 1995, 48 (07):
  • [20] Shrinkage Compensating Concrete for Bridge Decks
    Ramey, George E.
    Pittman, David W.
    Webster, Gregory K.
    Concrete International, 1999, 21 (04): : 29 - 34